Tc max
120.0 K
Tc ambient
—
arXiv year
2025
Papers
2
Tc exp.
—
Tc theo.
120.0 K
Evidence
theoretical
Tc max measured at theoretical (DFT/computational), P=30 GPa, arXiv:2512.19901, confirmed by 2 papers
Evidence (7 records from 2 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 120.0 | 30.0 | — | — | — | 2025 | T2 | 2512.19901 |
| 119.0 | 45.0 | — | — | — | 2025 | T2 | 2512.19901 |
| 118.0 | 50.0 | — | — | — | 2026 | T1 | DOI: 10.1103/9f4v-4bvs |
| 118.0 | 50.0 | — | — | — | 2025 | T2 | 2512.19901 |
| 118.0 | 40.0 | — | — | — | 2025 | T2 | 2512.19901 |
| 114.0 | 20.0 | — | — | — | 2025 | T2 | 2512.19901 |
| 110.0 | 50.0 | — | — | — | 2025 | T2 | 2512.19901 |
Hydride Tc parameters (26)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| YSbH6 | 132.0 | 20.0 | 3.44 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 114.0 | 20.0 | 3.44 | 0.23 | — | Eliashberg | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 114.0 | 20.0 | 3.44 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 114.0 | 20.0 | 3.44 | — | — | Allen-Dynes | 2025 | 2512.19901 |
| YSbH6 | 86.0 | 20.0 | 3.44 | 0.13 | — | Allen-Dynes | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 136.0 | 30.0 | 2.21 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 120.0 | 30.0 | 2.21 | 0.23 | — | Eliashberg | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 120.0 | 30.0 | 2.21 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 114.0 | 30.0 | 2.21 | 0.13 | — | Allen-Dynes | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 114.0 | 30.0 | 2.21 | — | — | Allen-Dynes | 2025 | 2512.19901 |
| YSbH6 | 130.0 | 40.0 | 1.95 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 118.0 | 40.0 | 1.95 | 0.23 | — | Eliashberg | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 118.0 | 40.0 | 1.95 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 108.0 | 40.0 | 1.95 | 0.13 | — | Allen-Dynes | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 108.0 | 40.0 | 1.95 | — | — | Allen-Dynes | 2025 | 2512.19901 |
| YSbH6 | 143.0 | 45.0 | 2.07 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 119.0 | 45.0 | 2.07 | 0.23 | — | Eliashberg | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 119.0 | 45.0 | 2.07 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 116.0 | 45.0 | 2.07 | 0.13 | — | Allen-Dynes | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 116.0 | 45.0 | 2.07 | — | — | Allen-Dynes | 2025 | 2512.19901 |
| YSbH6 | 150.5 | 50.0 | 2.34 | — | — | DFT | 2025 | 2512.19901 |
| YSbH6 | 135.0 | 50.0 | 1.95 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 118.0 | 50.0 | 1.95 | 0.23 | — | Eliashberg | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 118.0 | 50.0 | 1.95 | — | — | Eliashberg | 2025 | 2512.19901 |
| YSbH6 | 110.0 | 50.0 | 1.95 | 0.13 | — | Allen-Dynes | 2026 | DOI: 10.1103/9f4v-4bvs |
| YSbH6 | 110.0 | 50.0 | 1.95 | — | — | Allen-Dynes | 2025 | 2512.19901 |
Structure
- Crystal structure
- cubic
- Space group
- Pm-3
- Lattice a (Å)
- 3.666
Superconducting parameters
- λ_eph (e–ph coupling)
- 3.44