Tc max
113.0 K
Tc ambient
—
arXiv year
2024
Papers
2
Tc exp.
113.0 K
Tc theo.
110.0 K
Evidence
mixed
Tc max measured at P=191.7 GPa, polycrystal, resistivity, DOI: 10.1103/tjqv-vxrz
Evidence (2 records from 2 papers)
the flat columns above are aggregates — each line here is one paper's claim| Tc (K) | P (GPa) | Sample | Method | Pairing | Year | Tier | Paper |
|---|---|---|---|---|---|---|---|
| 113.0 | 191.7 | polycrystal | resistivity | — | 2026 | T1 | DOI: 10.1103/tjqv-vxrz |
| 110.0 | 140.0 | — | — | — | 2024 | T1 | DOI: 10.1103/PhysRevB.109.054512 |
Hydride Tc parameters (8)
independent NER enrichment for pressure, λ, μ*, and ω_log| Formula | Tc (K) | P (GPa) | λ | μ* | ω_log (K) | Method | Year | Paper |
|---|---|---|---|---|---|---|---|---|
| YScH8 | 124.4 | 100.0 | 1.80 | 0.05 | — | Eliashberg | 2025 | 2509.17501 |
| YScH8 | 104.3 | 100.0 | 1.80 | 0.05 | — | Eliashberg | 2025 | 2509.17501 |
| YScH8 | 110.2 | 140.0 | 1.54 | 0.10 | 817 | Allen-Dynes | 2024 | DOI: 10.1103/PhysRevB.109.054512 |
| YScH8 | 110.0 | 140.0 | — | — | — | DFT | 2026 | DOI: 10.1103/tjqv-vxrz |
| YScH8 | 97.0 | 171.0 | — | — | — | resistivity | 2026 | DOI: 10.1103/tjqv-vxrz |
| YScH8 | 116.0 | 190.0 | 1.35 | — | 1132 | Allen-Dynes | 2026 | DOI: 10.1103/tjqv-vxrz |
| YScH8 | 113.0 | 191.7 | — | — | — | resistivity | 2026 | DOI: 10.1103/tjqv-vxrz |
| YScH8 | 107.0 | 194.0 | — | — | — | resistivity | 2026 | DOI: 10.1103/tjqv-vxrz |
Structure
- Crystal structure
- P4/mmm
- Space group
- P4/mmm
Superconducting parameters
- λ_eph (e–ph coupling)
- —