Shoutao Zhang, Xin Du, Jianyan Lin, Aitor Bergara, Xin Chen, Xiaobing Liu, Xiaohua Zhang, Guochun Yang
DOI 10.1103/PhysRevB.101.174507 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The search for elemental allotropes is an active research field to get unusual structures with unique properties. The removal of metal atoms from pressure-induced stable binary compounds has become a useful method for obtaining elemental allotropes with interesting properties that otherwise would not be accessible at ambient pressure. Although three-dimensional boron allotropes have been studied extensively, none of those found so far are superconducting at ambient pressure. Here we propose that NaB4 and Na2B17 can be used as precursors to achieve superconducting boron allotropes at ambient pressure. First-principle swarm-intelligence structure search calculations identify several novel sodium borides (e.g., Na3B2,Na2B3,NaB4, and Na2B17) under high pressure. Interestingly, the B atoms in I4/mmmNaB4 and PmNa2B17 form three-dimensional frameworks with open channels, where Na atoms are located. After the removal of Na atoms, two hitherto unknown boron allotropes, named as I4/mmmB4 and PmB17, are stable at ambient pressure. They are metallic with superconducting critical temperatures of 19.8 and 15.4 K, respectively, becoming the highest ones among bulk boron allotropes. In addition, considering their predicted Vickers hardness of 27.3 and 26.8 GPa, they are also potential hard materials.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| B4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 19.8 | Pressure unresolved | unknown |
| B17 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 15.4 | Pressure unresolved | unknown |
| Si6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 12 | Pressure unresolved | unknown |
Similar papers
Superhard and superconducting boron clathrates in the prediction of U-B compounds
similarity 0.91Juefei Wu et al.
Source status unknown — claims are unverified
Modulation of superconductivity and superhardness in XB4C4 (X=Be,B,Al,Si,P, and Ti) borocarbides at ambient pressure
similarity 0.90Qiwen Jiang et al.
Source status unknown — claims are unverified
Van Hove singularity, flat bands, Dirac states, and superconductivity in van der Waals–bonded and covalently bonded bilayer borophene with a coloring triangular lattice
similarity 0.90Yan Liu et al.
Source status unknown — claims are unverified
High-temperature multigap superconductivity in two-dimensional metal borides
similarity 0.89Cem Sevik et al.
Source status unknown — claims are unverified
Superconductivity in compressed ternary alkaline boron hydrides
similarity 0.89Simin Li et al.
Source status unknown — claims are unverified
High-temperature superconductivity in M2BH6 hydrides under near ambient pressure
similarity 0.89Weiguo Sun et al.
Source status unknown — claims are unverified