Superconducting MgB2 thin films nano-bridges for cryo-electronic application
M. Gregor, R. Micunek, T. Plecenik, T. Roch, A. Lugstein, E. Bertagnolli, I. Vavra, M. Stefecka, M. Kubinec, M. Leporis, V. Gasparik, P. Kus, A. Plecenik
arXiv:0705.4229 · 2007-05-29 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin films in vacuum results in smooth superconducting MgB2 thin films with roughness below 10 nm, critical temperature Tcon = 31 K and transition width DTc less than 1 K. Nano-bridges based on the superconducting MgB2 thin films using optical and Focused Ion Beam lithography were prepared. Critical current density jc (4.2 K) measured on 50 nm wide strip was 7.3x106 A/cm2 and no significant loss of superconducting properties was detected. Resistance vs. temperature and critical current vs. temperature characteristics were measured on these structures using standard DC four probe measurements.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 31 | Pressure not reported | onset |
Similar papers
High critical current densities in superconducting MgB2 thin films
similarity 0.93S. H. Moon et al. · 2001 · arXiv:cond-mat/0104230
Source status unknown — claims are unverified
MgB2 superconductor thin films on Si and Al2O3 substrates
similarity 0.92A. Plecenik et al. · 2001 · arXiv:cond-mat/0105612
Source status unknown — claims are unverified
Electrical and structural properties of MgB2 films prepared by sequential deposition of B and Mg on the NbN buffered Si(100) substrate
similarity 0.92S. Chromik et al. · 2004 · arXiv:cond-mat/0401569
Source status unknown — claims are unverified
Superconducting properties of MgB2 thin films prepared on flexible plastic substrates
similarity 0.92P. Kus et al. · 2002 · arXiv:cond-mat/0206442
Source status unknown — claims are unverified
Growth of superconducting MgB2 thin films via postannealing techniques
similarity 0.92W. N. Kang et al. · 2002 · arXiv:cond-mat/0209226
Source status unknown — claims are unverified
Superconducting MgB(2) films via precursor post-processing approach
similarity 0.91M. Paranthaman et al. · 2001 · arXiv:cond-mat/0103569
Source status unknown — claims are unverified