Superconducting properties of MgB2 thin films prepared on flexible plastic substrates
P. Kus, A. Plecenik, L. Satrapinsky, Y. Xu, R. Sobolewski
arXiv:cond-mat/0206442 · DOI 10.1063/1.1507828 · 2002-06-24 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in an Ar or vacuum atmosphere. In the optimal annealing process, the Mg-B films were heated to approximately 600 C, but at the same time, the backside of the structures was attached to a water-cooled radiator to avoid overheating of the plastic substrate. The resulting MgB2 films were amorphous with the onset of the superconducting transition at T_(c,on) about 33 K and the transition width of approximately 3 K. The critical current density was > 7x10^5 A/cm^2 at 4.2 K, and its temperature dependence indicated a granular film composition with a network of intergranular weak links. The films could be deposited on large-area foils (up to 400 cm^2) and, after processing, cut into any shapes (e.g., stripes) with scissors or bent multiple times, without any observed degradation of their superconducting properties.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 33 | Pressure not reported | onset |
Similar papers
High critical current densities in superconducting MgB2 thin films
similarity 0.92S. H. Moon et al. · 2001 · arXiv:cond-mat/0104230
Source status unknown — claims are unverified
Superconducting MgB2 thin films nano-bridges for cryo-electronic application
similarity 0.92M. Gregor et al. · 2007 · arXiv:0705.4229
Source status unknown — claims are unverified
Superconducting properties of nanocrystalline MgB thin films made by an in situ annealing process
similarity 0.90X. H. Zeng et al. · 2001 · arXiv:cond-mat/0105080
Source status unknown — claims are unverified
MgB2 superconducting thin films with a transition temperature of 39 Kelvin
similarity 0.90W. N. Kang et al. · 2001 · arXiv:cond-mat/0104266
Source status unknown — claims are unverified
A sol-gel method for growing superconducting MgB2 films
similarity 0.90Liping Chen et al. · 2011 · arXiv:1102.5623
Source status unknown — claims are unverified
Superconducting MgB2 Thin Films with Tc of about 39K Grown by Pulsed Laser Deposition
similarity 0.90S. F. Wang et al. · 2001 · arXiv:cond-mat/0104555
Source status unknown — claims are unverified