Superconductivity of non- stoichiometric intermetallic compound NbB2
Monika Mudgel, V. P. S. Awana, G. L. Bhalla, H. Kishan
arXiv:0807.1198 · DOI 10.1016/j.ssc.2008.07.006 · 2008-07-08 · Solid State Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report the synthesis, magnetic susceptibility and crystal structure analysis for NbB2+x (x = 0.0 to 1.0) samples. The study facilitates in finding a correlation among the lattice parameters, chemical composition and the superconducting transition temperature Tc. Rietveld analysis is done on the X- ray diffraction patterns of all synthesized samples to determine the lattice parameters. The a parameter decreases slightly and has a random variation with increasing x, while c parameter increases from 3.26 for pure NbB2 to 3.32 for x=0.4 i.e. NbB2.4. With higher Boron content (x>0.4) the c parameter decreases slightly. The stretching of lattice in c direction induces superconductivity in the non- stoichiometric niobium boride. Pure NbB2 is non-superconductor while the other NbB2+x (x>0.0) samples show diamagnetic signal in the temperature range 8.9-11K. Magnetization measurements (M-H) at a fixed temperature of 5K are also carried out in both increasing and decreasing directions of field. The estimated lower and upper critical fields (Hc1 & Hc2) as viewed from M-H plots are around 590 and 2000Oe respectively for NbB2.6 samples. In our case, superconductivity is achieved in NbB2 by varying the Nb/B ratios, rather than changing the processing conditions as reported by others.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| NbB2.6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.95 | Pressure not reported | unknown |
Similar papers
Superconductivity of Various Borides: The Role of Stretched c- Parameter
similarity 0.91Monika Mudgel et al. · 2008 · arXiv:0811.4224
Source status unknown — claims are unverified
Evidence of unconventional superconductivity in the Ni-doped NbB2 system
similarity 0.91S. T. Renosto et al. · 2018 · arXiv:1810.09976
Source status unknown — claims are unverified
X-ray photoelectron spectroscopy studies of non-stoichiometric superconducting NbB2+x
similarity 0.88R. Escamilla & L. Huerta · 2004 · arXiv:cond-mat/0411131
Source status unknown — claims are unverified
Conventional Superconductivity properties of the ternary boron-nitride Nb2BN
similarity 0.86O. V. Cigarroa et al. · 2014 · arXiv:1401.0834
Source status unknown — claims are unverified
Enhanced Critical parameters of nano-Carbon doped MgB2 Superconductor
similarity 0.86Monika Mudgel et al. · 2009 · arXiv:0907.2129
Source status unknown — claims are unverified
Carbon substitution in MgB2 single crystals: structural and superconducting properties
similarity 0.85S. M. Kazakov et al. · 2004 · arXiv:cond-mat/0405060
Source status unknown — claims are unverified