Carbon substitution in MgB2 single crystals: structural and superconducting properties
S. M. Kazakov, R. Puzniak, K. Rogacki, A. V. Mironov, N. D. Zhigadlo, J. Jun, Ch. Soltmann, B. Batlogg, J. Karpinski
arXiv:cond-mat/0405060 · DOI 10.1103/PhysRevB.71.024533 · 2004-05-04 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Growth of carbon substituted magnesium diboride Mg(B1-xCx)2 single crystals with 0<x<0.15 is reported and the structural, transport, and magnetization data are presented. The superconducting transition temperature decreases monotonically with increasing carbon content in the full investigated range of substitution. By adjusting the nominal composition, Tc of substituted crystals can be tuned in a wide temperature range between 10 and 39 K. Simultaneous introduction of disorder by carbon substitution and significant increase of the upper critical field Hc2 is observed. Comparing with the non-substituted compound, Hc2 at 15K for x=0.05 is enhanced by more then a factor of 2 for H oriented both perpendicular and parallel to the ab-plane. This enhancement is accompanied by a reduction of the Hc2-anisotropy coefficient gamma from 4.5 (for non-substituted compound) to 3.4 and 2.8 for the crystals with x = 0.05 and 0.095, respectively. At temperatures below 10 K, the single crystal with larger carbon content shows Hc2 (defined at zero resistance) higher than 7 and 24 T for H oriented perpendicular and parallel to the ab-plane, respectively. Observed increase of Hc2 cannot be explained by the change in the coherence length due to disorder-induced decrease of the mean free path only.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | unknown |
Similar papers
Carbon substitution in MgB2 single crystals: Structural and superconducting properties
similarity 1.00S. M. Kazakov et al.
Source status unknown — claims are unverified
Systematic Effects of Carbon Doping on the Superconducting Properties of Mg(B1−xCx)2
similarity 0.94R. H. T. Wilke et al.
Source status unknown — claims are unverified
Enhancement of the irreversibility field by carbon substitution in single crystal MgB
similarity 0.93E. Ohmichi et al. · 2003 · arXiv:cond-mat/0312348
Source status unknown — claims are unverified
Influence of the carbon substitution on the critical current density and AC losses in MgB2 single crystals
similarity 0.92M. Ciszek et al. · 2011 · arXiv:1101.2596
Source status unknown — claims are unverified
Strongly enhancend anisotropic upper critical field in carbon substituted MgB2: impact of Fermi surface changes
similarity 0.92R. Puzniak et al. · 2004 · arXiv:cond-mat/0404579
Source status unknown — claims are unverified
Crystal Chemistry of Carbon-Substituted MgB2
similarity 0.91M. Avdeev et al. · 2003 · arXiv:cond-mat/0301025
Source status unknown — claims are unverified