Superconductivity in layered iron Selenide induced by cobalt- and sodium-doping
Zhanqiang Liu, Aihua Fang, Fuqiang Huang, Mianheng Jiang
arXiv:0808.1784 · 2008-08-13 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconductivity with zero resistance transition temperature (Tc) up to 8.4 K and 8.3 K can be obtained by doping cobalt and sodium in alfa-FeSe with the nominal composition of Fe0.92Co0.08Se and Na0.1FeSe, respectively. The electrical resistivity and AC magnetic susceptibility of the prepared samples, measured with physical property measurement system (PPMS), unambiguously consistent with each other to indicate that the samples are superconductive. The respective doping mechanisms for cobalt and sodium into the parent alfa-FeSe are the Fe-site substitution and the interlayer insertion. It is the first time that alfa-FeSe can be induced to be a superconductor with Na+ intercalated into the interlayers.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Fe0.92Co0.08Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.4 | Pressure not reported | zero_resistance |
| Fe0.92Co0.08Se Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.4 | Pressure not reported | zero_resistance |
| Na0.1FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.3 | Pressure not reported | zero_resistance |
| Na0.1FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.3 | Pressure not reported | zero_resistance |
Similar papers
Superconducting phases in (NH3)yMxFeSe1−zTez (M=Li,Na,andCa)
similarity 0.91Yusuke Sakai et al.
Source status unknown — claims are unverified
Enhanced superconductivity and anisotropy of FeTe0.6Se0.4 single crystals with Li-NH3 intercalation
similarity 0.89Chenghe Li et al. · 2017 · arXiv:1708.05310
Source status unknown — claims are unverified
Two new parent compounds for FeSe-based superconducting phases
similarity 0.88Shifeng Jin et al. · 2016 · arXiv:1607.01103
Source status unknown — claims are unverified
Synthesis and post-annealing effects of alkaline-metal-ethylenediamine-intercalated superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K
similarity 0.88Takashi Noji et al. · 2014 · arXiv:1408.0346
Source status unknown — claims are unverified
Pressure effects on superconducting properties of single-crystalline Co doped NaFeAs
similarity 0.88A. F. Wang et al. · 2012 · arXiv:1207.5382
Source status unknown — claims are unverified
Effect of doping on electrical, magnetic, and superconducting properties of KxFe2−yS2
similarity 0.88Jiangang Guo et al.
Source status unknown — claims are unverified