Superconducting Properties of adipic acid doped Bulk MgB2 Superconductor
Arpita Vajpayee, V. P. S. Awana, G. L. Bhalla, A. K. Nigam, H. Kishan
arXiv:0811.2646 · DOI 10.1088/0953-2048/22/1/015016 · 2008-11-17
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report the effect of adipic acid (C6H10O4) doping on lattice parameters, microstructure, critical temperature (Tc), current density (Jc), and irreversibility field (Hirr) for MgB2 superconductor. Actual carbon (C) substitution level for boron (B) is estimated to be from 0.40 percent to 2.95 percent for different doping levels. A reduction in Tc from 38.43 to 34.93 K and in lattice parameter a from 3.084(3) A to 3.075(6) Ais observed for the10 wt percent C6H10O4 doped sample in comparison to pristine MgB2. This is an indication of C substitution at boron sites, with the C coming from the decomposition of C6H10O4 at the time of reaction. Interestingly the doped samples have resulted in significant enhancement of Jc and Hirr. All the doped samples exhibit the Jc value of the order of 10^4 A/cm2 at 5 K and 8 T, which is higher by an order of magnitude as compared to undoped sample. This result indicates that C6H10O4 is a promising material for MgB2 for obtaining the excellent Jc values under higher magnetic fields.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 38.43 | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 34.93 | Pressure not reported | unknown |
Similar papers
Improvement of Critical Current Density and Upper Critical Field in MgB2 using Carbohydrate
similarity 0.90J. H. Kim et al. · 2006 · arXiv:cond-mat/0612472
Source status unknown — claims are unverified
Strong enhancement of critical current density in MgB2 superconductor using carbohydrate doping
similarity 0.89Kim, J. H. et al. · 2006 · arXiv:cond-mat/0607350
Source status unknown — claims are unverified
Effect of carbon nanotube doping on critical current density of MgB2 superconductor
similarity 0.87S. X. Dou et al. · 2003 · arXiv:cond-mat/0310196
Source status unknown — claims are unverified
Effect of PVA doping on flux pinning in Bulk MgB2
similarity 0.86Arpita Vajpayee et al. · 2007 · arXiv:0708.3885
Source status unknown — claims are unverified
Significant improvement of flux pinning and irreversibility field in nano-Carbon doped MgB2 superconductor
similarity 0.86Monika Mudgel et al. · 2008 · arXiv:0803.0373
Source status unknown — claims are unverified
Effect of nano-carbon particle doping on the flux pinning properties of MgB2 superconductor
similarity 0.86S. Soltanian et al. · 2003 · arXiv:cond-mat/0302530
Source status unknown — claims are unverified