Improvement of Critical Current Density and Upper Critical Field in MgB2 using Carbohydrate
J. H. Kim, M. S. A. Hossain, X. Xu, W. K. Yeoh, D. Q. Shi, S. X. Dou, S. Ryu, M. Rindfleisch, M. Tomsic
arXiv:cond-mat/0612472 · 2006-12-19 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We evaluated the doping effects of carbohydrate (malic acid, C4H6O5), from 0wt% to 30wt% of total MgB2, on the phase, lattice parameters, critical temperature, resistivity, and upper critical field of MgB2 superconductor. The lattice parameters calculated show a large decrease in the a-axis for MgB2 + C4H6O5 samples, but no change in the c-axis. This is an indication of the carbon substitution into boron coming from C4H6O5, resulting in enhancement of resistivity, critical current density, and upper critical field. Specifically, the critical current density value of 25000 Acm2 at 5 K and 8 T for the MgB2 + 30wt% C4H6O5 sample is higher than that of the un-doped MgB2 by a factor of 21. In addition, resistivity value for all the MgB2 + C4H6O5 samples ranged from 80 to 90 microohm centimeter at 40 K, which is higher than for un-doped MgB2. The increased resistivity indicates increased impurity scattering due to carbon, resulting in enhanced upper critical field.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Strong enhancement of critical current density in MgB2 superconductor using carbohydrate doping
similarity 0.94Kim, J. H. et al. · 2006 · arXiv:cond-mat/0607350
Source status unknown — claims are unverified
Superconducting Properties of adipic acid doped Bulk MgB2 Superconductor
similarity 0.90Arpita Vajpayee et al. · 2008 · arXiv:0811.2646
Source status unknown — claims are unverified
Systematic Effects of Carbon Doping on the Superconducting Properties of Mg(B1−xCx)2
similarity 0.88R. H. T. Wilke et al.
Source status unknown — claims are unverified
Properties of MgB2 thin films with carbon doping
similarity 0.88A. V. Pogrebnyakov et al. · 2004 · arXiv:cond-mat/0407146
Source status unknown — claims are unverified
Carbon substitution in MgB2 single crystals: Structural and superconducting properties
similarity 0.88S. M. Kazakov et al.
Source status unknown — claims are unverified
Carbon substitution in MgB2 single crystals: structural and superconducting properties
similarity 0.87S. M. Kazakov et al. · 2004 · arXiv:cond-mat/0405060
Source status unknown — claims are unverified