Conventional proximity effect in bilayers of superconducting underdoped $La_{1.88}Sr_{0.12}CuO_4$ islands coated with non superconducting overdoped $La_{1.65}Sr_{0.35}CuO_4$

G. Koren; O. Millo

doi:10.1103/PHYSREVB.80.054507

← Back to search

Conventional proximity effect in bilayers of superconducting underdoped $La_{1.88}Sr_{0.12}CuO_4$ islands coated with non superconducting overdoped $La_{1.65}Sr_{0.35}CuO_4$

G. Koren, O. Millo

arXiv:0904.1928 · DOI 10.1103/PHYSREVB.80.054507 · 2009-04-13 · Physical Review B

T1theoretical7 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Following a recent study by our group in which a large $T_c$ enhancement was reported in bilayers of the non-superconducting $La_{1.65}Sr_{0.35}CuO_4$ and superconducting $La_{1.88}Sr_{0.12}CuO_4$ films [Phys. Rev. Lett. \textbf{101}, 057005 (2008)], we checked if a similar effect occurs when superconducting $La_{1.88}Sr_{0.12}CuO_4$ islands are coated with a continuous layer of the non superconducting $La_{1.65}Sr_{0.35}CuO_4$. We found that no such phenomenon is observed. The bare superconducting islands film behaves as an insulator where transport occurs via hopping or tunneling between islands, but exhibits a weak signature of localized superconductivity at $\sim$18 K. When over coated with a $La_{1.65}Sr_{0.35}CuO_4$ film, it becomes superconducting with a $T_c$ onset of 16.6 K, which is less than that of a thick $La_{1.88}Sr_{0.12}CuO_4$ film (25.7 K). We therefore conclude that the lower $T_c$ in the bilayer is due to a conventional proximity effect.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	18	Pressure unresolved	unknown
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16.6	Pressure unresolved	onset
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25.7	Pressure unresolved	unknown
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15.6	Pressure unresolved	onset
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	11.6	Pressure unresolved	midpoint
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.3	Pressure unresolved	zero_resistance
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16.6	Pressure unresolved	onset
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15.3	Pressure unresolved	midpoint
La1.88Sr0.12CuO4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13.7	Pressure unresolved	zero_resistance