Synthesis, characterization and low temperature studies of iron chalcogenide superconductors

J. Janaki; T. Geetha Kumary; Awadhesh Mani; S. Kalavathi; G V R Reddy; G. V. Narasimha Rao; A. Bharathi

doi:10.1002/CHIN.201005004

← Back to search

Synthesis, characterization and low temperature studies of iron chalcogenide superconductors

J. Janaki, T. Geetha Kumary, Awadhesh Mani, S. Kalavathi, G V R Reddy, G. V. Narasimha Rao, A. Bharathi

arXiv:0904.3851 · DOI 10.1002/CHIN.201005004 · 2009-04-24 · arXiv: Superconductivity

T1experimental39 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We have synthesized tetragonal iron selenide and telluride superconductors through solid state reaction at 450deg.C and 550deg.C respectively. These synthesis temperatures have been established by optimization. Electrical resistivity and magnetic susceptibility measurements (4.2-300 K) confirm superconductivity with Tc of around 8.5 K in all selenide samples of nominal composition Fe1+deltaSe (delta=0.02-0.22). However, Scanning Electron Microscopy/ Energy Dispersive Spectroscopy studies clearly indicate that the actual stoichiometric ratio of Fe : Se for all the samples synthesized is around 1:1. Also all the samples exhibit identical phase transition temperatures from tetragonal to orthorhombic structure below ~ 100 K implying identical phase composition. The partial substitution of Se by Te leads to an enhancement of Tc to ~ 13 K. The non-superconducting telluride Fe1.09Te exhibits a metal-insulator phase transition at ~ 82 K. Substitution studies of this telluride system by S and Si have in addition been carried out to investigate if chemical pressure induces superconductivity.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	unknown
FeSe1-xTex Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	Pressure not reported	unknown
FeSe1-xTex Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	Pressure not reported	unknown