Synthesis, crystal structure and chemical stability of the superconductor FeSe_{1-x}

Ekaterina Pomjakushina; Kazimierz Conder; Vladimir Pomjakushin; Markus Bendele; Rustem Khasanov

doi:10.1103/PhysRevB.80.024517

← Back to search

Synthesis, crystal structure and chemical stability of the superconductor FeSe_{1-x}

Ekaterina Pomjakushina, Kazimierz Conder, Vladimir Pomjakushin, Markus Bendele, Rustem Khasanov

arXiv:0905.2115 · DOI 10.1103/PhysRevB.80.024517 · 2009-05-13 · Physical Review B

T1theoretical112 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report on a comparative study of the crystal structure and the magnetic properties of FeSe1-x (x= 0.00 - 0.15) superconducting samples by neutron powder diffraction and magnetization measurements. The samples were synthesized by two different methods: a 'low-temperature' one using powders as a starting material at T =700 C and a "high-temperature' method using solid pieces of Fe and Se at T= 1070 C. The effect of a starting (nominal) stoichiometry on the phase purity of the obtained samples, the superconducting transition temperature Tc, as well as the chemical instability of FeSe1-x at ambient conditions were investigated. It was found that in the Fe-Se system a stable phase exhibiting superconductivity at Tc~8K exists in a narrow range of selenium concentration (FeSe0.974(2)).

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe0.974 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure unresolved	unknown
FeSe1-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	unknown
FeSe0.99 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	unknown
FeSe0.98 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5	Pressure not reported	unknown
FeSe0.97 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	0.6	Pressure not reported	unknown