Synthesis, phase stability, structural and physical properties of 11-type iron chalcogenides

Sahana Rößler; Cevriye Koz; Steffen Wirth; Ulrich Schwarz

doi:10.1002/pssb.201600149

← Back to search

Synthesis, phase stability, structural and physical properties of 11-type iron chalcogenides

Sahana Rößler, Cevriye Koz, Steffen Wirth, Ulrich Schwarz

arXiv:1606.01012 · DOI 10.1002/pssb.201600149 · 2016-06-03 · physica status solidi (b)

T4review12 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

This article reviews recent experimental investigations on two binary Fe-chalcogenides: FeSe and Fe$_{1+y}$Te. The main focus is on synthesis, single crystal growth, chemical composition, as well as on the effect of excess iron on structural, magnetic, and transport properties of these materials. The structurally simplest Fe-based superconductor Fe$_{1+x}$Se with a critical temperature $T_c \approx$ 8.5 K undergoes a tetragonal to orthorhombic phase transition at a temperature $T_s \approx$ 87 K. No long-range magnetic order is observed down to the lowest measured temperature in Fe$_{1+x}$Se. On the other hand, isostructural Fe$_{1+y}$Te displays a complex interplay of magnetic and structural phase transitions in dependence on the tuning parameter such as excess amount of Fe or pressure, but it becomes a superconductor only when Te is substituted by a sufficient amount of Se. We summarize experimental evidence for different competing interactions and discuss related open questions.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Fe1+xSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure unresolved	unknown
Fe1+yTe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37	Pressure not reported	unknown
Fe1+ySe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown