Diamagnetism and Cooper pairing above $T_c$ in cuprates

Lu Li; Yayu Wang; Seiki Komiya; Shimpei Ono; Yoichi Ando; G. D. Gu; N. P. Ong

doi:10.1103/PhysRevB.81.054510

← Back to search

Diamagnetism and Cooper pairing above $T_c$ in cuprates

Lu Li, Yayu Wang, Seiki Komiya, Shimpei Ono, Yoichi Ando, G. D. Gu, N. P. Ong

arXiv:0906.1823 · DOI 10.1103/PhysRevB.81.054510 · 2009-06-09 · Physical Review B

T1theoretical253 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In the cuprate superconductors, Nernst and torque magnetization experiments have provided evidence that the disappearance of the Meissner effect at $T_c$ is caused by the loss of long-range phase coherence, rather than the vanishing of the pair condensate. Here we report a series of torque magnetization measurements on single crystals of $\mathrm{La_{2-x}Sr_xCuO_4}$ (LSCO), $\mathrm{Bi_2Sr_{2-y}La_yCuO_6}$ (Bi 2201), $\mathrm{Bi_2Sr_2CaCu_2O_{8+δ}}$ (Bi 2212) and optimal $\mathrm{YBa_2Cu_3O_7}$. Some of the measurements were taken to fields as high as 45 T. Focusing on the magnetization above $T_c$, we show that the diamagnetic term $M_d$ appears at an onset temperature $T^M_{onset}$ high above $T_c$. We construct the phase diagram of both LSCO and Bi 2201 and show that $T^M_{onset}$ agrees with the onset temperature of the vortex Nernst signal $T^ν_{onset}$. Our results provide thermodynamic evidence against a recent proposal that the high-temperature Nernst signal in LSCO arises from a quasiparticle contribution in a charge-ordered state.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Bi2Sr1.3La0.7CuO6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	12	Pressure not reported	unknown
Bi2Sr1.4La0.6CuO6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	18	Pressure not reported	unknown
Bi2Sr1.56La0.44CuO6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	unknown
Bi2Sr1.8La0.2CuO6 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	20	Pressure not reported	unknown
Bi2Sr2CaCu2O8+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	88	Pressure not reported	unknown
Bi2Sr2CaCu2O8+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	50	Pressure not reported	unknown
YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	92	Pressure not reported	unknown
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	39	Pressure not reported	unknown
Mg0.75B2Al0.25 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25	Pressure not reported	unknown