Upper critical field, lower critical field and critical current density of FeTe0.60Se0.40 single crystal

C S Yadav; P L Paulose

doi:10.1088/1367-2630/11/10/103046

← Back to search

Upper critical field, lower critical field and critical current density of FeTe0.60Se0.40 single crystal

C S Yadav, P L Paulose

arXiv:0907.0147 · DOI 10.1088/1367-2630/11/10/103046 · 2009-07-01 · New Journal of Physics

T1theoretical119 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The transport and magnetic studies are performed on high quality FeTe0.60Se0.40 single crystals to determine the upper critical fields (Hc2), lower critical field (Hc1) and the Critical current density (Jc). The value of upper critical field Hc2 are very large, whereas the activation energy as determined from the slope of the Arrhenius plots are was found to be lower than that in the FeAs122 superconductor. The lower critical field was determined in ab direction and c direction of the crystal, and was found to have a anisotropy of 'gamma'{=(Hc1//c) / (Hc1//b)} ~ 4. The magnetic isotherms measured up to 12 Tesla shows the presence of fishtail behavior. The critical current densities at 1.8K of the single crystal was found to almost same in both ab and c direction as 1X105 Amp/cm2 in low field regime.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeTe0.60Se0.40 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	—
FeTe0.60Se0.40 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	—