Low-temperature Synthesis of FeTe0.5Se0.5 Polycrystals with a High Transport Critical Current Density

Qing-Ping Ding; Shyam Mohan; Yuji Tsuchiya; Toshihiro Taen; Yasuyuki Nakajima; Tsuyoshi Tamegai

doi:10.1088/0953-2048/24/7/075025

← Back to search

Low-temperature Synthesis of FeTe0.5Se0.5 Polycrystals with a High Transport Critical Current Density

Qing-Ping Ding, Shyam Mohan, Yuji Tsuchiya, Toshihiro Taen, Yasuyuki Nakajima, Tsuyoshi Tamegai

arXiv:1103.1809 · DOI 10.1088/0953-2048/24/7/075025 · 2011-03-09 · Superconductor Science and Technology

T336 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We have prepared high-quality polycrystalline FeTe0.5Se0.5 at temperature as low as 550°C. The transport critical current density evaluated by the current-voltage characteristics is over 700 A/cm2 at 4.2 K under zero field, which is several times larger than FeTe0.5Se0.5 superconducting wires. The critical current density estimated from magneto-optical images of flux penetration is also similar to this value. The upper critical field of the polycrystalline FeTe0.5Se0.5 at T = 0 K estimated by Werthamer-Helfand-Hohenberg theory is 585 kOe, which is comparable to that of single crystals. This study gives some insight into how to improve the performance of FeTe0.5Se0.5 superconducting wires.