Magneto-optical characterizations of FeTe$_{0.5}$Se$_{0.5}$ thin films with critical current density over 1 MA/cm$^2$

Yue Sun; Yuji Tsuchiya; Sunseng Pyon; Tsuyoshi Tamegai; Cheng Zhang; Toshinori Ozaki; Qiang Li

doi:10.1088/0953-2048/28/1/015010

← Back to search

Magneto-optical characterizations of FeTe$_{0.5}$Se$_{0.5}$ thin films with critical current density over 1 MA/cm$^2$

Yue Sun, Yuji Tsuchiya, Sunseng Pyon, Tsuyoshi Tamegai, Cheng Zhang, Toshinori Ozaki, Qiang Li

arXiv:1412.2454 · DOI 10.1088/0953-2048/28/1/015010 · 2014-12-08

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We performed magneto-optical (MO) measurements on FeTe$_{0.5}$Se$_{0.5}$ thin films grown on LaAlO$_3$ (LAO) and Yttria-stabilized zirconia (YSZ) single-crystalline substrates. These thin films show superconducting transition temperature, ${T_c}$ $\sim$ 19 K, 4 K higher than the bulk sample. Typical roof-top patterns can be observed in the MO images of thin films grown on LAO and YSZ, from which a large and homogeneous critical current density, ${J_c}$, over 1 $\times$ 10$^6$ A/cm$^2$ at 5 K was obtained. Magnetic flux penetration measurement reveals that the current is almost isotropically distributed in the two thin films. Compared with bulk crystals, FeTe$_{0.5}$Se$_{0.5}$ thin film demonstrates not only higher ${T_c}$, but also much larger ${J_c}$, which is attractive for applications.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeTe0.5Se0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	19	Pressure not reported	unknown
FeTe0.6Se0.4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15	Pressure not reported	unknown