T. Ozaki, K. Deguchi, Y. Mizuguchi, H. Kumakura, Y. Takano
arXiv:1012.1404 · DOI 10.1016/j.physc.2011.05.146 · 2010-12-07 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We fabricated FeTe0.5Se0.5 superconducting wires using ex-situ Powder-in-tube method with an Fe sheath. It was amazing that superconducting current was observed in the as-drawn wire without any heat treatments. By heat treatment at 200C for 2 hours, Tczero and Jc at 4.2 K were enhanced up to 9.1 K and 64.1 A/cm2 (Ic = 182.6 mA), respectively. Furthermore, the Jc of FeTe0.5Se0.5 wire heat treated at 200C for 2 hours was not much sensitive to the applied magnetic fields. Therefore, FeTe0.5Se0.5 wires have a great potential for applications.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeTe0.5Se0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.1 | Pressure not reported | zero_resistance |
Similar papers
Transport properties of iron-based FeTe0.5Se0.5 superconducting wire
similarity 0.96T. Ozaki et al. · 2010 · arXiv:1008.1447
Source status unknown — claims are unverified
Fabrication of binary FeSe superconducting wires by novel diffusion process
similarity 0.93Toshinori Ozaki et al. · 2011 · arXiv:1103.3602
Source status unknown — claims are unverified
Enhancement of superconducting properties in FeSe wires using a quenching technique
similarity 0.91Toshinori Ozaki et al. · 2011 · arXiv:1112.4119
Source status unknown — claims are unverified
Transport properties of the single- and 3-core Fe-Se wires fabricated by a novel chemical-transformation PIT process
similarity 0.91Yoshikazu Mizuguchi et al. · 2011 · arXiv:1106.3383
Source status unknown — claims are unverified
Superconducting properties of FeSe wires and tapes prepared by gas diffusion technique
similarity 0.89Zhaoshun Gao et al. · 2011 · arXiv:1103.5304
Source status unknown — claims are unverified
Fabrication and transport properties of Sr0.6K0.4Fe2As2 multifilamentary superconducting wires
similarity 0.89Chao Yao et al. · 2012 · arXiv:1212.5873
Source status unknown — claims are unverified