T. Ozaki, K. Deguchi, Y. Mizuguchi, H. Kumakura, Y. Takano
arXiv:1008.1447 · DOI 10.1016/j.physc.2011.05.018 · 2010-08-09
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
FeTe0.5Se0.5 superconducting wires have been fabricated using ex-situ PIT method with an Fe sheath. Among the other FeAs-based superconductor, FeTe0.5Se0.5 has great advantage for application due to binary composition and less toxic. Surprisingly, superconducting current was observed in the as-fabricated wire without any heat treatments. Zero resistivity and transport critical current density (Jc) were 3.2 K and 2.8 A/cm2, respectively. In addition, by annealing at 200 degC for 2 h, critical temperature Tczero and Jc were enhanced up to 9.1 K, and 64.1 A/cm2, respectively. This suggests that the grain connectivity was improved by heat treatment, and superconducting property of FeTe0.5Se0.5 wire was enhanced.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeTe0.5Se0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 3.2 | Pressure not reported | zero_resistance |
| FeTe0.5Se0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.1 | Pressure not reported | zero_resistance |
Similar papers
Microstructure and transport properties of FeTe0.5Se0.5 superconducting wires fabricated by ex-situ Powder-in-tube process
similarity 0.96T. Ozaki et al. · 2010 · arXiv:1012.1404
Source status unknown — claims are unverified
Low-temperature Synthesis of FeTe0.5Se0.5 Polycrystals with a High Transport Critical Current Density
similarity 0.92Qing-Ping Ding et al. · 2011 · arXiv:1103.1809
Source status unknown — claims are unverified
Enhancement of superconducting properties in FeSe wires using a quenching technique
similarity 0.91Toshinori Ozaki et al. · 2011 · arXiv:1112.4119
Source status unknown — claims are unverified
Fabrication of the iron-based superconducting wire using Fe(Se, Te)
similarity 0.91Yoshikazu Mizuguchi et al. · 2009 · arXiv:0906.1636
Source status unknown — claims are unverified
Magneto-optical characterizations of FeTeSe thin films with critical current density over 1 MA/cm
similarity 0.91Yue Sun et al. · 2014 · arXiv:1412.2454
Source status unknown — claims are unverified
Critical Current Density and AC Magnetic Susceptibility of High-quality FeTeSe Superconducting Tapes
similarity 0.90Xin Zhou et al. · 2025 · arXiv:2501.16189
Source status unknown — claims are unverified