Superconducting properties of FeSe wires and tapes prepared by gas diffusion technique
Zhaoshun Gao, Yanpeng Qi, Lei Wang, Dongliang Wang, Xianping Zhang, Chao Yao, Yanwei Ma
arXiv:1103.5304 · DOI 10.1088/0953-2048/24/6/065022 · 2011-03-28 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconducting FeSe in the form of wires and tapes were successfully fabricated using a novel gas diffusion procedure. Structural analysis by mean of x-ray diffraction shows that themain phase of tetragonal PbO-type FeSe was obtained by this synthesis method. The zero resistivity transition temperature of the FeSe was confirmed to be 9.3 K. The critical current density as high as 137 A/cm^2 (4 K, self field) has been observed. The results suggest that the diffusion procedure is promising in preparing high-quality FeSe wires and tapes.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 9.3 | Pressure not reported | zero_resistance |
Similar papers
Magneto-optical imaging and transport properties of FeSe superconducting tapes prepared by diffusion method
similarity 0.93Q. P. Ding et al. · 2011 · arXiv:1109.1921
Source status unknown — claims are unverified
Transport properties of the single- and 3-core Fe-Se wires fabricated by a novel chemical-transformation PIT process
similarity 0.90Yoshikazu Mizuguchi et al. · 2011 · arXiv:1106.3383
Source status unknown — claims are unverified
Microstructure and transport properties of FeTe0.5Se0.5 superconducting wires fabricated by ex-situ Powder-in-tube process
similarity 0.89T. Ozaki et al. · 2010 · arXiv:1012.1404
Source status unknown — claims are unverified
Low-temperature Synthesis of FeTe0.5Se0.5 Polycrystals with a High Transport Critical Current Density
similarity 0.89Qing-Ping Ding et al. · 2011 · arXiv:1103.1809
Source status unknown — claims are unverified
Flux free growth of superconducting FeSe single crystals
similarity 0.89P. K. Maheshwari et al. · 2016 · arXiv:1606.08201
Source status unknown — claims are unverified
Evolution of Superconductivity in FeTeSe Annealed in Te Vapor
similarity 0.88Yue Sun et al. · 2013 · arXiv:1308.4480
Source status unknown — claims are unverified