A new approach for improving global critical current density in Fe(Se0.5Te0.5) polycrystalline materials
A. Palenzona, A. Sala, C. Bernini, V. Braccini, M. R. Cimberle, C. Ferdeghini, G. Lamura, A. Martinelli, I. Pallecchi, G. Romano, M. Tropeano, R. Fittipaldi, A. Vecchione, A. Polyanskii, F. Kametani, M. Putti
arXiv:1205.3618 · DOI 10.1088/0953-2048/25/11/115018 · 2012-05-16 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A novel method to prepare bulk Fe(Se0.5Te0.5) samples is presented, based on a melting process and a subsequent annealing treatment. With respect to the standard sintering technique, it produces much more homogeneous and denser samples, characterized by large and well interconnected grains. The resulting samples exhibit optimal critical temperature values, sharp resistive and magnetic transitions, large magnetic hysteresis loops and high upper critical fields are observed. Interestingly, the global critical current density is much enhanced as compared to the values reported in literature for bulk samples of the same 11 family, reaching about 103 A/cm2 at zero field at 4.2 K as assessed by magnetic, transport and magneto-optical techniques. Even more importantly, its field dependence turns out to be very weak, such that at μ_{0}H = 7 T it is suppressed only by a factor \sim2.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Fe(Se0.5Te0.5) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Fe(Se0.5Te0.5) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Low-temperature Synthesis of FeTe0.5Se0.5 Polycrystals with a High Transport Critical Current Density
similarity 0.90Qing-Ping Ding et al. · 2011 · arXiv:1103.1809
Source status unknown — claims are unverified
Effect of substitution and heat treatment route on polycrystalline FeSe0.5Te0.5 Superconductors
similarity 0.87Hacisalihoglu, Muammer Yasin & Yanmaz, Ekrem · 2012 · arXiv:1206.0401
Source status unknown — claims are unverified
Bulk Superconductivity in Fe1+yTe0.6Se0.4 Induced by Removal of Excess Fe
similarity 0.86Wei Zhou et al. · 2014 · arXiv:1405.6818
Source status unknown — claims are unverified
Significant enhancement of critical current density in H+-intercalated FeSe single crystal
similarity 0.85Yan Meng et al. · 2023 · arXiv:2303.11601
Source status unknown — claims are unverified
Critical Current Density and AC Magnetic Susceptibility of High-quality FeTeSe Superconducting Tapes
similarity 0.85Xin Zhou et al. · 2025 · arXiv:2501.16189
Source status unknown — claims are unverified
Cometal addition effect on superconducting properties and granular behaviours of polycrystalline FeSe0.5Te0.5
similarity 0.85Manasa, Manasa et al. · 2023 · arXiv:2308.01367
Source status unknown — claims are unverified