Scaling behaviour of the critical current in clean epitaxial Ba(Fe1-xCox)2As2 thin films

Iida, K.; Haenisch, J.; Thersleff, T.; Kurth, F.; Kidszun, M.; Haindl, S.; Huehne, R.; Schultz, L.; Holzapfel, B.

Scaling behaviour of the critical current in clean epitaxial Ba(Fe1-xCox)2As2 thin films

Iida, K., Haenisch, J., Thersleff, T., Kurth, F., Kidszun, M., Haindl, S., Huehne, R., Schultz, L., Holzapfel, B.

arXiv:1001.2505 · 2010-03-16

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The angular-dependent critical current density, Jc(theta), and the upper critical field, Hc2(theta), of epitaxial Ba(Fe1-xCox)2As2 thin films have been investigated. No Jc(theta) peaks for H || c were observed regardless of temperatures and magnetic fields. In contrast, Jc(theta) showed a broad maximum at theta=90 degree, which arises from intrinsic pinning. All data except at theta=90 degree can be scaled by the Blatter plot. Hc2(theta) near Tc follows the anisotropic Ginzburg-Landau expression. The mass anisotropy increased from 1.5 to 2 with increasing temperature, which is an evidence for multi-band superconductivity.