Unusually high critical current of clean P-doped BaFe2As2 single crystalline thin film
F. Kurth, C. Tarantini, V. Grinenko, J. Haenisch, J. Jaroszynski, E. Reich, Y. Mori, A. Sakagami, T. Kawaguchi, J. Engelmann, L. Schultz, B. Holzapfel, H. Ikuta, R. Huehne, K. Iida
arXiv:1502.05345 · DOI 10.1063/1.4908257 · 2015-02-18 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Microstructura lly clean, isov alently P-doped BaFe2As2 (Ba-122) single crystalline thin films have been prepared on MgO (001) substrates by molecular beam epitaxy. These films show a superconducting transition temperature (Tc) of over 30 K although P content is around 0.22, which is lower than the optimal one for single crystals (i.e., 0.33). The enhanced Tc at this doping level is attributed to the in-plane tensile strain. The strained film shows high transport self-field critical current densities (Jc) of over 6 MA/cm2 at 4.2 K, which are among the highest for Fe based superconductors (FeSCs). In-field Jc exceeds 0.1 MA/cm2 at m0H = 35 T for H||ab and m0H = 18 T for H||c at 4.2 K, respectively, in spite of moderate upper critical fields compared to other FeSCs with similar Tc. Structural investigations reveal no defects or misoriented grains pointing to strong pinning centers. We relate this unexpected high Jc to a strong enhancement of the vortex core energy at optimal Tc, driven by in-plane strain and doping. These unusually high Jc make P-doped Ba-122 very favorable for high-field magnet applications.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| BaFe2(As0.78P0.22)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 30.7 | Pressure not reported | onset |
Similar papers
Electrodynamics of superconducting pnictide superlattices
similarity 0.91A. Perucchi et al. · 2014 · arXiv:1404.4299
Source status unknown — claims are unverified
Enhanced critical-current in P-doped BaFe2As2 thin films on metal substrates arising from poorly aligned grain boundaries
similarity 0.90Hikaru Sato et al. · 2016 · arXiv:1606.01477
Source status unknown — claims are unverified
One-dimensional pinning behavior in Co-doped BaFe2As2 thin films
similarity 0.90V. Mishev et al. · 2014 · arXiv:1401.7518
Source status unknown — claims are unverified
High Critical Current Density 4 MA/cm2 in Co-Doped BaFe2As2 Epitaxial Films Grown on (La, Sr)(Al, Ta)O3 Substrates without Buffer Layers
similarity 0.89Takayoshi Katase et al. · 2010 · arXiv:1005.2023
Source status unknown — claims are unverified
High-field transport properties of a P-doped BaFe2As2 film on technical substrate
similarity 0.89Kazumasa Iida et al. · 2017 · arXiv:1701.04154
Source status unknown — claims are unverified
BaFe2(As1-xPx)2 (x = 0.22-0.42) thin films grown on practical metal-tape substrates and their critical current densities
similarity 0.89Hidenori Hiramatsu et al. · 2017 · arXiv:1703.06393
Source status unknown — claims are unverified