BaFe2(As1-xPx)2 (x = 0.22-0.42) thin films grown on practical metal-tape substrates and their critical current densities
Hidenori Hiramatsu, Hikaru Sato, Toshio Kamiya, Hideo Hosono
arXiv:1703.06393 · DOI 10.1088/1361-6668/aa621c · 2017-03-19 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We optimized the substrate temperature (Ts) and phosphorus concentration (x) of BaFe2(As1-xPx)2 films on practical metal-tape substrates for pulsed laser deposition from the viewpoints of crystallinity, superconductor critical temperature (Tc), and critical current density (Jc). It was found that the optimum Ts and x values are 1050 degree C and x = 0.28, respectively. The optimized film exhibits Tc_onset = 26.6 and Tc_zero = 22.4 K along with a high self-field Jc at 4 K (~1 MA/cm2) and relatively isotropic Jc under magnetic fields up to 9 T. Unexpectedly, we found that lower crystallinity samples, which were grown at a higher Ts of 1250 degree C than the optimized Ts = 1050 degree C, exhibit higher Jc along the ab plane under high magnetic fields than the optimized samples. The presence of horizontal defects that act as strong vortex pinning centers, such as stacking faults, are a possible origin of the high Jc values in the poor crystallinity samples.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| BaFe2(As1-xPx)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 26.6 | Pressure not reported | onset |
| BaFe2(As1-xPx)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 22.4 | Pressure not reported | zero_resistance |
Similar papers
High critical-current density with less anisotropy in BaFe2(As,P)2 epitaxial thin films: Effect of intentionally grown c-axis vortex-pinning centers
similarity 0.92Hikaru Sato et al. · 2014 · arXiv:1403.1947
Source status unknown — claims are unverified
Enhanced critical-current in P-doped BaFe2As2 thin films on metal substrates arising from poorly aligned grain boundaries
similarity 0.92Hikaru Sato et al. · 2016 · arXiv:1606.01477
Source status unknown — claims are unverified
Unusually high critical current of clean P-doped BaFe2As2 single crystalline thin film
similarity 0.90F. Kurth et al. · 2015 · arXiv:1502.05345
Source status unknown — claims are unverified
Doping Dependence of the Second Magnetization Peak, Critical Current Density and Pinning Mechanism in BaFeNiAs Pnictide Superconductors
similarity 0.89Shyam Sundar et al. · 2019 · arXiv:1901.10049
Source status unknown — claims are unverified
Achievement of practical level critical current densities in PIT Ba1-xKxFe2As2/Ag tapes by conventional cold mechanical deformation
similarity 0.89Zhaoshun Gao et al. · 2013 · arXiv:1310.4623
Source status unknown — claims are unverified
Grain boundary characteristics of Fe-based superconductors
similarity 0.88Kazumasa Iida et al. · 2020 · arXiv:2003.09146
Source status unknown — claims are unverified