Uniaxial strain detwinning of CaFe2As2 and BaFe2As2: optical and transport study

Abstract

TThe parent compounds of iron-arsenide superconductors, $A$Fe$_{2}$As$_{2}$ ($A$=Ca, Sr, Ba), undergo a tetragonal to orthorhombic structural transition at a temperature $T_{\mathrm{TO}}$ in the range 135 to 205K depending on the alkaline earth element. Below $T_{\mathrm{TO}}$ the free standing crystals split into equally populated structural domains, which mask intrinsic, in-plane, anisotropic properties of the materials. Here we demonstrate a way of mechanically detwinning CaFe$_{2}$As$_{2}$ and BaFe$_{2}$As$_{2}$. The detwinning is nearly complete, as demonstrated by polarized light imaging and synchrotron $X$-ray measurements, and reversible, with twin pattern restored after strain release. Electrical resistivity measurements in the twinned and detwinned states show that resistivity, $ρ$, decreases along the orthorhombic $a_{o}$-axis but increases along the orthorhombic $b_{o}$-axis in both compounds. Immediately below $T_{\mathrm{TO}}$ the ratio $ρ_{bo}/ ρ_{ao}$ = 1.2 and 1.5 for Ca and Ba compounds, respectively. Contrary to CaFe$_{2}$As$_{2}$, BaFe$_{2}$As$_{2}$ reveals an anisotropy in the nominally tetragonal phase, suggesting that either fluctuations play a larger role above $T_{\mathrm{TO}}$ in BaFe$_{2}$As$_{2}$ than in CaFe$_{2}$As$_{2}$, or that there is a higher temperature crossover or phase transition.

Similar papers