Evolution of superconductivity by oxygen annealing in FeTe0.8S0.2

Yoshikazu Mizuguchi; Keita Deguchi; Shunsuke Tsuda; Takahide Yamaguchi; Yoshihiko Takano

doi:10.1209/0295-5075/90/57002

← Back to search

Evolution of superconductivity by oxygen annealing in FeTe0.8S0.2

Yoshikazu Mizuguchi, Keita Deguchi, Shunsuke Tsuda, Takahide Yamaguchi, Yoshihiko Takano

arXiv:1003.2059 · DOI 10.1209/0295-5075/90/57002 · 2010-03-10 · EPL (Europhysics Letters)

T1theoretical58 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Oxygen annealing dramatically improved the superconducting properties of solid-state-reacted FeTe0.8S0.2, which showed only a broad onset of superconducting transition just after the synthesis. The zero resistivity appeared and reached 8.5 K by the oxygen annealing at 200\degree C. The superconducting volume fraction was also enhanced from 0 to almost 100%. The lattice constants were compressed by the oxygen annealing, indicating that the evolution of bulk superconductivity in FeTe0.8S0.2 was correlated to the shrinkage of lattice.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeTe0.8S0.2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	zero_resistance