Structural behavior of Pb$_y$Bi$_{1.95-y}$Sr$_{1.49}$La$_{0.4}$Cu$_{1.15}$O$_{6+δ}$ for 0<y<0.53

Abstract

In the Bi cuprates, the presence of a near 1$\times$5 superstructure is well known. Usually, this superstructure is suppressed by the substitution of lead, but there have been reports of a phase separation in so called α and β phases. This paper shows in high detail time how and why the phase separation develops and what happens to the quasi-1$\times$5 superstructure upon lead substitution. For this purpose, the lanthanum- and lead-substituted single-layered superconductor Bi$_{2+z}$Sr$_{2-z}$CuO$_{6+δ}$ has been investigated by scanning tunneling microscopy and low-energy electron diffraction. The La content was kept constant at slightly under-doped concentration while the Pb content was changed systematically. Thermodynamic considerations show that a phase mixture of α and β phases is inevitable.