Takayoshi Katase, Yoshihiro Ishimaru, Akira Tsukamoto, Hidenori Hiramatsu, Toshio Kamiya, Keiichi Tanabe, Hideo Hosono
arXiv:1011.5721 · DOI 10.1038/ncomms1419 · 2010-11-26 · Nature Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
High critical temperature superconductors have zero power consumption and could be used to produce ideal electric power lines. The principal obstacle in fabricating superconducting wires and tapes is grain boundaries-the misalignment of crystalline orientations at grain boundaries, which is unavoidable for polycrystals, largely deteriorates critical current density. Here, we report that High critical temperature iron pnictide superconductors have advantages over cuprates with respect to these grain boundary issues. The transport properties through well-defined bicrystal grain boundary junctions with various misorientation angles (thetaGB) were systematically investigated for cobalt-doped BaFe2As2 (BaFe2As2:Co) epitaxial films fabricated on bicrystal substrates. The critical current density through bicrystal grain boundary (JcBGB) remained high (> 1 MA/cm2) and nearly constant up to a critical angle thetac of ~9o, which is substantially larger than the thetac of ~5o for YBCO. Even at thetaGB > thetac, the decay of JcBGB was much smaller than that of YBCO.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| BaFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| YBa2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Weak-link behavior of grain boundaries in superconducting Ba(Fe1-xCox)2As2 bicrystals
similarity 0.91S. Lee et al. · 2009 · arXiv:0907.3741
Source status unknown — claims are unverified
Fabrication of grain boundary junctions using NdFeAs(O,F) superconducting thin films
similarity 0.90Taito Omura et al. · 2017 · arXiv:1712.05966
Source status unknown — claims are unverified
High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
similarity 0.89J. D. Weiss et al. · 2012 · arXiv:1204.4426
Source status unknown — claims are unverified
Iron-Based Superconductors: A Decade of Materials, Magnetism, and Mechanisms
similarity 0.89Xingye Lu et al. · 2026 · arXiv:2607.11355
Source status unknown — claims are unverified
Highly textured oxypnictide superconducting thin films on metal substrates
similarity 0.88Kazumasa Iida et al. · 2014 · arXiv:1410.8743
Source status unknown — claims are unverified
Biaxially textured cobalt-doped BaFe2As2 films with high critical current density over 1 MA/cm2 on MgO-buffered metal-tape flexible substrates
similarity 0.88Takayoshi Katase et al. · 2011 · arXiv:1103.5815
Source status unknown — claims are unverified