Superconductivity and Magnetic Properties of high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs)

J. J. Ying; X. F. Wang; X. G. Luo; A. F. Wang; M. Zhang; Y. J. Yan; Z. J. Xiang; R. H. Liu; P. Cheng; G. J. Ye; X. H. Chen

doi:10.1103/PhysRevB.83.212502

Superconductivity and Magnetic Properties of high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs)

J. J. Ying, X. F. Wang, X. G. Luo, A. F. Wang, M. Zhang, Y. J. Yan, Z. J. Xiang, R. H. Liu, P. Cheng, G. J. Ye, X. H. Chen

arXiv:1012.5552 · DOI 10.1103/PhysRevB.83.212502 · 2010-12-27 · Physical Review B

T1theoretical10 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting transition temperatures ($T_{\rm c}$) of 31 K and 30 K for K- and Cs-compounds, respectively, with nearly 100% shielding fraction. The crystals show quite high resistivity in the normal state of more than 160 m$Ω$ cm and 1300 m$Ω$ cm maximum resistivity for $K_{0.86}Fe_2Se_{1.82}$ and $Cs_{0.86}Fe_{1.66}Se_{2}$ single crystals, respectively. Much larger upper critical field $H_{\rm c2}$ is inferred from low-temperature iso-magnetic-field magnetoresistance in these crystals than in FeSe. The anisotropy $H^{ab}_{\rm c2}$(0)/$H^{c}_{\rm c2}$(0) is around 3 for both of the two materials. Anisotropic peculiar magnetic behavior in normal state has been found for $Cs_{0.86}Fe_{1.66}Se_{2}$

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
K0.86Fe2Se1.82 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	31	Pressure not reported	onset
K0.86Fe2Se1.82 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	28.7	Pressure not reported	zero_resistance
K0.86Fe2Se1.82 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	29	Pressure not reported	onset
Cs0.86Fe1.66Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	onset
Cs0.86Fe1.66Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26.5	Pressure not reported	zero_resistance
Cs0.86Fe1.66Se2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25.5	Pressure not reported	onset
LaFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure unresolved	unknown
SmFeAs(O,F) Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	43	Pressure unresolved	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure unresolved	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37	4.5 GPa	onset
KFeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure unresolved	onset
CsFeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	27	Pressure unresolved	onset