Shilpam Sharma, Jai Prakash, Gohil S. Thakur, A. T. Satya, A. Bharathi, A K Ganguli, C S Sundar
arXiv:1104.0137 · DOI 10.1088/0953-2048/24/6/065020 · 2011-04-01 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
PrOFe0.9Co0.1As is known to be a superconductor with a TC of ~14 K. In an attempt to induce charge transfer and also induce chemical pressure between the FeAs and PrO layers we have synthesized for the first time oxypnictides of the type PrOFe0.9Co0.1As1-xPx (P doping at As sites). All the compounds crystallize in the tetragonal ZrCuSiAs type structure (space group = P4/nmm). The lattice parameters (a and c) decrease as expected on substitution of smaller phosphorous at the arsenic site in PrOFe0.9Co0.1As and a decrease in TC was observed on substitution of P ions at a low rate of 0.13K/at. % of P for x > 0.1. The irreversibility field (Hirr) and critical current density (JC), obtained using the AC susceptibility measurements was found to decrease monotonically with increasing 'P' concentration. 'Hirr' is observed to be much smaller than HC2, pointing to a very low pinning energy. The pinning potential obtained using both in-field transport and AC susceptibility measurements indicate a low value of ~40 meV and show no significant variation with P substitution.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| PrOFe0.9Co0.1As Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 14 | Pressure not reported | unknown |
Similar papers
Evolution of superconductivity in PrFe1-xCoxAsO with x = 0.0 to 1.0
similarity 0.89Poonam Rani et al. · 2014 · arXiv:1402.1601
Source status unknown — claims are unverified
Effects of high-pressure synthesis on phase formation and superconducting properties of PrFeAsO1-xFx
similarity 0.88Priya Singh et al. · 2026 · arXiv:2608.08083
Source status unknown — claims are unverified
Flux pinning in (1111) iron-pnictide superconducting crystals
similarity 0.88C. J. van der Beek et al. · 2010 · arXiv:1003.3936
Source status unknown — claims are unverified
The magnetization of PrFeAsOF$_{0.12} sueprconductor
similarity 0.87D. Bhoi et al. · 2010 · arXiv:1002.0208
Source status unknown — claims are unverified
Superconductivity at 11.3 K induced by cobalt doping in CeOFeAs
similarity 0.87J. Prakash et al. · 2008 · arXiv:0810.1364
Source status unknown — claims are unverified
Normal-state transport properties of PrFeAsOF superconductor
similarity 0.87D. Bhoi et al. · 2008 · arXiv:0807.3833
Source status unknown — claims are unverified