Epitaxial growth of FeSe$_{0.5}$Te$_{0.5}$ thin films on CaF$_2$ substrates with high critical current density

I. Tsukada; M. Hanawa; T. Akiike; F. Nabeshima; Y. Imai; A. Ichinose; S. Komiya; T. Hikage; T. Kawaguchi; H. Ikuta; A. Maeda

doi:10.1143/APEX.4.053101

Epitaxial growth of FeSe$_{0.5}$Te$_{0.5}$ thin films on CaF$_2$ substrates with high critical current density

I. Tsukada, M. Hanawa, T. Akiike, F. Nabeshima, Y. Imai, A. Ichinose, S. Komiya, T. Hikage, T. Kawaguchi, H. Ikuta, A. Maeda

arXiv:1104.0477 · DOI 10.1143/APEX.4.053101 · 2011-04-04 · Applied Physics Express

T1theoretical85 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In-situ epitaxial growth of FeSe$_{0.5}$Te$_{0.5}$ thin films is demonstrated on a non-oxide substrate CaF$_2$. Structural analysis reveals that compressive stress is moderately added to 36-nm thick FeSe$_{0.5}$Te$_{0.5}$, which pushes up the critical temperature above 15 K, showing higher values than that of bulk crystals. Critical current density at $T$ = 4.5 K reaches 5.9 x 10$^4$ Acm$^{-2}$ at $μ_0H$ = 10 T, and 4.2 x 10$^4$ Acm$^{-2}$ at $μ_0H$ = 14 T. These results indicate that fluoride substrates have high potential for the growth of iron-based superconductors in comparison with popular oxide substrates.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16.1	Pressure unresolved	midpoint
FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15.2	Pressure unresolved	zero_resistance
FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16.3	Pressure unresolved	midpoint
FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15.3	Pressure unresolved	zero_resistance
FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	21	Pressure unresolved	onset
FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure unresolved	unknown