Gap Anisotropy in Iron-Based Superconductors: A Point-Contact Andreev Reflection Study of BaFe$_{2-x}$Ni$_{x}$As$_2$ Single Crystals

Cong Ren; Zhao-Sheng Wang; Zhen-Yu Wang; Hui-Qian Luo; Xing-Ye Lu; Bin Sheng; Chun-Hong Li; Lei Shan; Huan Yang; Hai-Hu Wen

doi:10.1103/PhysRevB.86.060508

Gap Anisotropy in Iron-Based Superconductors: A Point-Contact Andreev Reflection Study of BaFe$_{2-x}$Ni$_{x}$As$_2$ Single Crystals

Cong Ren, Zhao-Sheng Wang, Zhen-Yu Wang, Hui-Qian Luo, Xing-Ye Lu, Bin Sheng, Chun-Hong Li, Lei Shan, Huan Yang, Hai-Hu Wen

arXiv:1106.2891 · DOI 10.1103/PhysRevB.86.060508 · 2011-06-15 · Physical Review B

T1theoretical6 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We report a systematic investigation on c-axis point-contact Andreev reflection (PCAR) in BaFe$_{2-x}$Ni$_x$As$_2$ superconducting single crystals from underdoped to overdoped regions (0.075 $\leq x\leq 0.15$). At optimal doping ($x=0.1$) the PCAR spectrum feature the structures of two superconducting gap and electron-boson coupling mode. In the $s\pm$ scenario, quantitative analysis using a generalized Blonder-Tinkham-Klapwijk (BTK) formalism with two gaps: one isotropic and another angle dependent, suggest a nodeless state in strong-coupling limit with gap minima on the Fermi surfaces. Upon crossing above the optimal doping ($x > 0.1$), the PCAR spectrum show an in-gap sharp narrow peak at low bias, in contrast to the case of underdoped samples ($x < 0.1$), signaling the onset of deepened gap minima or nodes in the superconducting gap. This result provides evidence of the modulation of the gap amplitude with doping concentration, consistent with the calculations for the orbital dependent pair interaction mediated by the antiferromagnetic spin fluctuations.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
BaFe1.925Ni0.075As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	onset
BaFe1.925Ni0.075As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
BaFe1.915Ni0.085As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	onset
BaFe1.915Ni0.085As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
BaFe1.9Ni0.1As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	onset
BaFe1.9Ni0.1As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
BaFe1.88Ni0.12As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	onset
BaFe1.88Ni0.12As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
BaFe1.85Ni0.15As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	onset
BaFe1.85Ni0.15As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown