Density effect on critical current density and flux pinning properties of polycrystalline SmFeAsO1-xFx superconductor
Y. Ding, Y. Sun, J. C. Zhuang, L. J. Cui, Z. X. Shi, Z. A. Ren
arXiv:1110.4532 · 2011-10-20
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A series of polycrystalline SmFeAs1-xOx bulks was prepared to systematically investigate the influence of sample density on flux pinning properties. Different sample densities were achieved by controlling the pelletizing pressure. The superconducting volume fraction, the critical current densities Jcm and the flux pinning force densities Fp were estimated from the magnetization measurements. Experimental results manifest that: (1) the superconducting volume fraction decreases with the decreasing of sample density. (2) The Jcm values have the similar trend except for the sample with very high density may due to different connectivity and pinning mechanism. Moreover, The Jcm(B) curve develops a peak effect at approximately the same field at which the high-density sample shows a kink. (3) The Fp(B) curve of the high-density sample shows a low-field peak and a high-field peak at several temperatures, which can be explained by improved intergranular current, while only one peak can be observed in Fp(B) of the low-density samples. Based on the scaling behaviour of flux pinning force densities, the main intragranular pinning is normal point pinning.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Strong enhancement of critical current density in both low & high fields and flux pinning mechanism under hydrostatic pressure in optimally doped (Ba,K)Fe2As2 single crystals
similarity 0.87Babar Shabbir et al. · 2015 · arXiv:1511.05638
Source status unknown — claims are unverified
Statistical variations of the elementary flux-pinning force and their effect on the shape of the bulk-pinning-force curve of high-field superconductors
similarity 0.87L. D. Cooley et al.
Source status unknown — claims are unverified
Oxypnictide SmFeAs(O,F) superconductor: a candidate for high-field magnet applications
similarity 0.87Kazumasa Iida et al. · 2013 · arXiv:1307.1282
Source status unknown — claims are unverified
Enhancement of transport critical current density of SmFeAsO1-xFx tapes fabricated by an ex-situ powder-in-tube method with a Sn-presintering process
similarity 0.87Qianjun Zhang et al. · 2014 · arXiv:1405.6835
Source status unknown — claims are unverified
Magnetization relaxation and collective vortex pinning in the Fe-based superconductor SmFeAsO0.9F0.1
similarity 0.87Huan Yang et al.
Source status unknown — claims are unverified
Flux pinning in (1111) iron-pnictide superconducting crystals
similarity 0.86C. J. van der Beek et al. · 2010 · arXiv:1003.3936
Source status unknown — claims are unverified