Flux pinning characteristics in cylindrical ingot niobium used in superconducting radio frequency cavity fabrication
Asavari S. Dhavale, Pashupati Dhakal, Anatolii A. Polyanskii, Gianluigi Ciovati
arXiv:1201.3857 · DOI 10.1088/0953-2048/25/6/065014 · 2012-01-18
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We present the results of from DC magnetization and penetration depth measurements of cylindrical bulk large-grain (LG) and fine-grain (FG) niobium samples used for the fabrication of superconducting radio frequency (SRF) cavities. The surface treatment consisted of electropolishing and low temperature baking as they are typically applied to SRF cavities. The magnetization data were fitted using a modified critical state model. The critical current density Jc and pinning force Fp are calculated from the magnetization data and their temperature dependence and field dependence are presented. The LG samples have lower critical current density and pinning force density compared to FG samples which implies a lower flux trapping efficiency. This effect may explain the lower values of residual resistance often observed in LG cavities than FG cavities.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Nb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Muon spin rotation studies of niobium for superconducting RF applications
similarity 0.89A. Grassellino et al. · 2013 · arXiv:1303.6480
Source status unknown — claims are unverified
Muon spin rotation studies of niobium for superconducting rf applications
similarity 0.89A. Grassellino et al.
Source status unknown — claims are unverified
RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide
similarity 0.88Eric Lechner et al. · 2021 · arXiv:2106.06647
Source status unknown — claims are unverified
Trapped magnetic flux in superconducting niobium samples
similarity 0.87S. Aull et al.
Source status unknown — claims are unverified
Simulation of nonlinear superconducting rf losses derived from characteristic topography of etched and electropolished niobium surfaces
similarity 0.87Chen Xu et al.
Source status unknown — claims are unverified
Plasma processing of large curved surfaces for superconducting rf cavity modification
similarity 0.86J. Upadhyay et al.
Source status unknown — claims are unverified