RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide
Eric Lechner, Jonathan Angle, Fred Stevie, Michael Kelley, Charles Reece, Ari Palczewski
arXiv:2106.06647 · DOI 10.1063/5.0059464 · 2021-06-12
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Recently, Nb superconducting radio frequency cavities vacuum heat treated between 300-400 C for a few hours have exhibited very high quality factors (~5x10^10 at 2.0 K). New secondary ion mass spectrometry measurements of O, N and C show this enhancement in RF surface conductivity is primarily associated with interstitial O alloying via dissolution and diffusion of the native oxide. We use a theory of oxide decomposition and O diffusion to quantify previously unknown parameters crucial in modeling this process. RF measurements of a vacuum heat treated Nb superconducting radio frequency cavity confirm the minimized surface resistance (higher Q0) previously expected only from 800 C diffusive alloying with N.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Nb Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Niobium thin film deposition studies on copper surfaces for superconducting radio frequency cavity applications
similarity 0.90W. M. Roach et al.
Source status unknown — claims are unverified
Niobium near-surface composition during nitrogen infusion relevant for superconducting radio-frequency cavities
similarity 0.90G. D. L. Semione et al.
Source status unknown — claims are unverified
Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity
similarity 0.89P. Dhakal et al. · 2012 · arXiv:1210.6875
Source status unknown — claims are unverified
Improvement and protection of niobium surface superconductivity by Atomic Layer Deposition and heat treatment
similarity 0.89T. Proslier et al. · 2008 · arXiv:0808.3427
Source status unknown — claims are unverified
Plasma processing of large curved surfaces for superconducting rf cavity modification
similarity 0.88J. Upadhyay et al.
Source status unknown — claims are unverified
Plasma treatment of bulk niobium surface for superconducting rf cavities: Optimization of the experimental conditions on flat samples
similarity 0.88M. Rašković et al.
Source status unknown — claims are unverified