Structure and Charge transfer Mechanism in Y1-xCaxBa2Cu3O7-δ through direct doping
Shiva Kumar Singh, M. Husain, V. P. S. Awana
arXiv:1202.5825 · 2012-02-27 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Here we study the effect of Ca doping on charge transfer mechanism of polycrystalline YBa2Cu3O7-δ compound. The samples of composition Y1-xCaxBa2Cu3O7-δ (x = 0.00, 0.05, 0.10, 0.20 and 0.30) are synthesized through standard solid state reaction route. Carrier doping is controlled by annealing of samples in oxygen and subsequently in reducing atmosphere. Samples are investigated using resistivity, dc magnetization (M-T) and magnetization with field (M-H) measurements. With increase of Ca the transition temperature (Tc) decreases in oxygenated samples, whereas the same increases in reduced samples. Further reduction of samples at higher temperatures (> 600 0C) though results in non-superconducting nature up to Ca concentration of x = 0.20, the x = 0.30 sample is superconducting below 30K. This provides a remarkably simple and effective way to study the relationship between structure, superconductivity, and associated electronic properties. Variations in Cu1-O4, Cu2-O4 and Cu2-O2 bond lengths with oxygen content, is seen through the structural refinement of XRD pattern. The effective coordination of Cu2 atom with oxygen changes with the change in theses bond lengths and hence the holes in the CuO2 planes. The charge transfer mechanism from CuOx chains to CuO2 planes and thus effective hole doping is discussed in context of observed results.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Y0.7Ca0.3Ba2Cu3O7-δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 30 | Pressure not reported | unknown |
Similar papers
Systematic induction of superconductivity in Y1-xCaxBa2Cu3O6.3 system
similarity 0.93V. P. S. Awana et al. · 2004 · arXiv:cond-mat/0403230
Source status unknown — claims are unverified
The role of Ca in superconducting and magnetic properties of Y1-xCaxBa2Cu3O7 (x = 0.0-0.30)
similarity 0.93N. P. Liyanawaduge et al. · 2011 · arXiv:1106.3144
Source status unknown — claims are unverified
Revival of Superconductivity by Y3+/Ca2+ substitution in YBa2Cu2.7Co0.3O7 without reported phase transformation
similarity 0.92M. A. Ansari et al. · 2004 · arXiv:cond-mat/0412152
Source status unknown — claims are unverified
Effects of Substituting Calcium for Yttrium on the Superconducting Properties of YBa2Cu3Oz Bulk Samples
similarity 0.90E. K. Nazarova et al. · 2004 · arXiv:cond-mat/0401584
Source status unknown — claims are unverified
Control of the hole concentration in the YBa2Cu3O6+z-type superconductors (Yb,Ca)(Ba,Sr)2Cu3O6+z with low and high Ca contents
similarity 0.90Takahiro Wada et al.
Source status unknown — claims are unverified
Mechanisms of Electrical Conductivity in Y(1-x)CaxBa2Cu3O6.1 System
similarity 0.90P. Starowicz & A. Szytula · 2004 · arXiv:cond-mat/0410763
Source status unknown — claims are unverified