Revival of Superconductivity by Y3+/Ca2+ substitution in YBa2Cu2.7Co0.3O7 without reported phase transformation
M. A. Ansari, Rashmi Nigam, V. P. S. Awana, Anurag Gupta, R. B. Saxena, H. Kishan, N. P. Lalla, V. Ganesan, A. V. Narlikar, C A. Cardoso
arXiv:cond-mat/0412152 · DOI 10.1063/1.1850383 · 2004-12-07 · Journal of Applied Physics
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Results of phase formation, resistivity (r), and thermo-electric power (S), are reported on Y1-xCaxBa2Cu2.7Co0.3O7 compounds with x = 0.1 and 0.2. Pristine compound i.e. without Co or Ca substitution crystallizes in orthorhombic structure with space group P/mmm. Cu-site Co substituted compound i.e. YBa2Cu2.7Co0.3O7 is tetragonal. With simultaneous doping of Ca at Y site in Co substituted compound i.e. Y1-xCaxBa2Cu2.7Co0.3O7 the tetragonal nature still remains. r(T) measurements showed superconducting transition temperature (Tc) to decrease from 90K (YBa2Cu3O7) to 33 K for YBa2Cu2.7Co0.3O7 which with further Ca substitution increases from 33K to 53K (Y0.9 Ca0.1Ba2Cu2.7Co0.3O7) and 67 K for Y0.8 Ca0.2Ba2Cu2.7Co0.3O7. Tc decreases first with Cu-site Co substitution by hole-filling and later recovers by simultaneous hole creation by Y site Ca substitution. Room temperature thermoelectric power S(300 K), which is an indirect measure of mobile carriers shows the decrease of carriers with Co doping and creation by Ca substitution. Our results demonstrate the hole filling by Co substitution is compensated by simultaneous Ca substitution.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| YBa2Cu3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 90 | Pressure not reported | unknown |
| YBa2Cu2.7Co0.3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 33 | Pressure not reported | unknown |
| Y0.9Ca0.1Ba2Cu2.7Co0.3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 53 | Pressure not reported | unknown |
| Y0.8Ca0.2Ba2Cu2.7Co0.3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 67 | Pressure not reported | unknown |
Similar papers
Role of calcium in suppressing the superconductivity of Y1−xCaxBa2Cu3O7−δ
similarity 0.92V. P. S. Awana & A. V. Narlikar
Source status unknown — claims are unverified
Magnetic doping effects on the superconductivity of Y1-xMxBa2Cu3O7-d (M = Fe, Co, Ni)
similarity 0.91Hamideh Shakeripour et al. · 2021 · arXiv:2101.09292
Source status unknown — claims are unverified
Mechanisms of Electrical Conductivity in Y(1-x)CaxBa2Cu3O6.1 System
similarity 0.90P. Starowicz & A. Szytula · 2004 · arXiv:cond-mat/0410763
Source status unknown — claims are unverified
Synthesis and superconducting properties of Y(Ba1−yLay)2Cu4O8 and (Y1−xCax)(Ba1−yLay)2Cu4O8
similarity 0.90Takeshi Sakurai et al.
Source status unknown — claims are unverified
The pseudogap in hole-doped cuprates: possible insights from the Kondo effect
similarity 0.88J. R. Cooper · 2021 · arXiv:2108.02108
Source status unknown — claims are unverified
Effects of Bi(x) additives on microstructure and superconductivity in YBa2−xBixCu3O7−δ
similarity 0.88Shanker Ram & K. A. Narayan
Source status unknown — claims are unverified