Magnetic doping effects on the superconductivity of Y1-xMxBa2Cu3O7-d (M = Fe, Co, Ni)
Hamideh Shakeripour, Seyed Sajjad Hosseini, Seyedeh Sara Ghotb, Behnaz Hadi-Sichani, Sepideh Pourasad
arXiv:2101.09292 · DOI 10.1016/j.ceramint.2020.12.176 · 2021-01-22
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The discovery of superconductivity in copper oxide compounds has attracted considerable attention over the past three decades. The high transition temperature in these compounds, exhibiting proximity to an antiferromagnetic order in their phase diagrams, remains one of the main areas of research. The present study attempts to introduce Fe, Co and Ni magnetic impurities into the superconducting Y-123 with the aim of exploring the transition temperature behavior. The solid-state synthesis is exploited to prepare fully oxygenated Y1-xMxBa2Cu3O7 (M = Co, Fe, Ni) samples with low levels of doping (0< x < 0.03). Systematic measurements are then employed to assess the synthesized samples using AC magnetic susceptibility, electrical resistivity and X-ray diffraction. The measurements revealed an increase in Tc as a result of magnetic substitution for Y. However, the study of non-magnetic dopings on the fully oxygenated Y1-xM'xBa2Cu3O7 (M' = Ca, Sr) samples showed a decrease in Tc. Quantitative XRD analysis further suggested that the internal pressure could have minor effects on the increase in Tc. The normal state resistivity vs temperature showed a linear profile, confirming that the samples are at an optimal doping of the carrier concentration.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Y1-xMxBa2Cu3O7-d Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Y1-xMxBa2Cu3O7-d Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Y1-xM'xBa2Cu3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| Y1-xM'xBa2Cu3O7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Effect of Fe on the superconductivity of the Ba-Y-Cu oxide system
similarity 0.92B. R. Zhao et al.
Source status unknown — claims are unverified
Magnetic order and superconductivity in YBa2Cu3−yMyOz (M=Fe,Co)
similarity 0.92D. Hechel et al.
Source status unknown — claims are unverified
Influence of Fe impurities on the Y-Ba-Cu-O superconducting system
similarity 0.92M. Mehbod et al.
Source status unknown — claims are unverified
Modification of the oxygen-isotope effect in high-temperature superconductors due to transition-metal doping
similarity 0.90H. J. Bornemann et al.
Source status unknown — claims are unverified
Effects of substitution of O by S and Cu by Fe on superconductivity in YBa2Cu3O7
similarity 0.90I. Felner et al.
Source status unknown — claims are unverified
Influence of magnetic rare-earth ion substitution on the magnetic susceptibility of high-Tc superconductors
similarity 0.90F. Zuo et al.
Source status unknown — claims are unverified