Synthesis of a new alkali metal-organic solvent intercalated iron selenide superconductor with Tc{\approx}45K
A. Krzton-Maziopa, E. V. Pomjakushina, V. Yu. Pomjakushin, F. von Rohr, A. Schilling, K. Conder
arXiv:1206.7022 · DOI 10.1088/0953-8984/24/38/382202 · 2012-06-29 · Journal of Physics: Condensed Matter
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report on a new iron selenide superconductor with a TC onset of 45K and the nominal composition Lix(C5H5N)yFe2-zSe2, synthesized via intercalation of dissolved alkaline metal in anhydrous pyridine at room temperature. This superconductor exhibits a broad transition, reaching zero resistance at 10K. Magnetization measurements reveal a superconducting shielding fraction of approximately 30%. Analogous phases intercalated with Na, K and Rb were also synthesized and characterized. The superconducting transition temperature of Lix(C5H5N)yFe2-zSe2 is clearly enhanced in comparison to the known superconductors FeSe0.98 (Tc ~ 8K) and AxFe2-ySe2 (TC ~ 27-32K) and is in close agreement with critical temperatures recently reported for Lix(NH3)yFe2-zSe2. Post-annealing of intercalated material (Lix(C5H5N)yFe2-zSe2) at elevated temperatures drastically enlarges the c-parameter of the unit cell (~44%) and increases the amount of superconducting shielding fraction to nearly 100%. Our findings indicate a new synthesis road leading to possibly even higher critical temperatures in this class of materials by intercalation of organic compounds between Fe-Se layers.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Lix(C5H5N)yFe2-zSe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 45 | Pressure not reported | onset |
| Lix(C5H5N)yFe2-zSe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10 | Pressure not reported | zero_resistance |
| FeSe0.98 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8 | Pressure not reported | unknown |
| AxFe2-ySe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Enhancement of superconducting transition temperature of FeSe by intercalation of a molecular spacer layer
similarity 0.93Matthew Burrard-Lucas et al. · 2012 · arXiv:1203.5046
Source status unknown — claims are unverified
Observation of superconductivity at 30 K~46 K in AxFe2Se2 (A = Li, Na, Ba, Sr, Ca, Yb, and Eu)
similarity 0.92T. P. Ying et al. · 2012 · arXiv:1202.4340
Source status unknown — claims are unverified
Synthesis and post-annealing effects of alkaline-metal-ethylenediamine-intercalated superconductors Ax(C2H8N2)yFe2-zSe2 (A = Li, Na) with Tc = 45 K
similarity 0.91Takashi Noji et al. · 2014 · arXiv:1408.0346
Source status unknown — claims are unverified
Magnetic phase separation and superfluid density measurements in alkali metal-organic solvent intercalated iron selenide superconductor Lix(C5H5N)yFe2-zSe2
similarity 0.91P. K. Biswas et al. · 2012 · arXiv:1209.5279
Source status unknown — claims are unverified
Superconducting phases in (NH3)yMxFeSe1−zTez (M=Li,Na,andCa)
similarity 0.90Yusuke Sakai et al.
Source status unknown — claims are unverified
Superconductivity at Tc = 44 K in LixFe2Se2(NH3)y
similarity 0.90E. -W. Scheidt et al. · 2012 · arXiv:1205.5731
Source status unknown — claims are unverified