Specific Heat Discontinuity DeltaC vs Tc in Annealed Ba(Fe1-xCox)2As2
J. S. Kim, B. D. Faeth, G. R. Stewart
arXiv:1208.2492 · DOI 10.1103/PhysRevB.86.054509 · 2012-08-13 · Physical Review B
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The low temperature specific heat of annealed single crystal samples of Ba(Fe1-xCox)2As2 with compositions spanning the entire superconducting phase diagram was measured. Effort was made to discover the best annealing schedule to maximize Tc and minimize transition width in these samples. Values of deltaC/Tc normalized to 100% superconducting volume fractions varied proportionally to Tc^alpha. Within a rather narrow error bar of +-0.15, the exponent alpha was the same (approximately 2) over a range of compositions (0.055 < x < 0.15) around the optimal concentration, x=0.08, where Tc is the maximum in the phase diagram. Thus, whether the superconductivity was coexistent with magnetism (underdoped) or not (overdoped) did not affect the non-BCS variation (alpha nearly 2 instead of 0.8-0.9 for BCS superconductors) of deltaC/Tc with Tc. The annealed samples in the present work, with increased deltaC/Tc and Tc values compared to previous results for the Ba(Fe1-xCox)2As2 alloy system, suggest that the intrinsic value of the exponent alpha for the iron superconductors, when the samples are annealed, with fewer defects, may indeed be even further from the BCS value of 0.8-0.9 than previously thought.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Ba(Fe1-xCox)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Specific heat jump at the superconducting transition temperature in Ba(Fe(1-x)Cox)2As2 and Ba(Fe(1-x)Nix)2As2 single crystals
similarity 0.91Sergey L. Bud'ko et al. · 2009 · arXiv:0905.2955
Source status unknown — claims are unverified
Doping-dependent specific heat study of the superconducting gap in Ba(Fe1−xCox)2As2
similarity 0.91K. Gofryk et al.
Source status unknown — claims are unverified
Effect of annealing on the specific heat of Ba(Fe1-xCox)2As2
similarity 0.90K. Gofryk et al. · 2010 · arXiv:1009.1091
Source status unknown — claims are unverified
Anisotropic thermodynamic and transport properties of single crystalline (BaK)FeAs (x = 0 and 0.45)
similarity 0.90N. Ni et al. · 2008 · arXiv:0806.1874
Source status unknown — claims are unverified
The electronic specific heat of Ba1-xKxFe2As2 from 2K to 380K
similarity 0.90J. G. Storey et al. · 2010 · arXiv:1001.0474
Source status unknown — claims are unverified
The influence of spin fluctuations on the thermal conductivity in superconducting Ba(Fe_{1-x}Co_x)_2As_2
similarity 0.90Andrew F. May et al. · 2013 · arXiv:1308.1907
Source status unknown — claims are unverified