Simultaneous measurement of pressure evolution of crystal structure and superconductivity in FeSe0.92 using designer diamonds
Uhoya, Walter, Tsoi, Georgiy, Vohra, Yogesh, Wolanyk, Nathaniel, Rao, Sistla Muralidhara, Wu, Maw-Kuen, Weir, Samuel
arXiv:1210.3645 · DOI 10.1209/0295-5075/99/26002 · 2012-10-16
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Simultaneous high pressure x-ray diffraction and electrical resistance measurements have been carried out on a PbO type α-FeSe0.92 compound to a pressure of 44 GPa and temperatures down to 4 K using designer diamond anvils at synchrotron source. At ambient temperature, a structural phase transition from a tetragonal (P4/nmm) phase to an orthorhombic (Pbnm) phase is observed at 11 GPa and the Pbnm phase persists up to 74 GPa. The superconducting transition temperature (TC) increases rapidly with pressure reaching a maximum of ~28 K at ~ 6 GPa and decreases at higher pressures, disappearing completely at 14.6 GPa. Simultaneous pressure-dependent x-ray diffraction and resistance measurements at low temperatures show superconductivity only in a low pressure orthorhombic (Cmma) phase of the α-FeSe0.92. Upon increasing pressure at 10 K near TC, crystalline phases change from a mixture of orthorhombic (Cmma) and hexagonal (P63/mmc) to a high pressure orthorhombic (Pbnm) phase near 6.4 GPa where TC is maximum.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe0.92 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 28 | 6.4 GPa | unknown |
Similar papers
Collapse of Metallicity and High- Superconductivity in the High-Pressure phase of FeSeS
similarity 0.89Pascal Reiss et al. · 2022 · arXiv:2212.06824
Source status unknown — claims are unverified
Effect of pressure on the structural phase transition and superconductivity in (Ba1−xKx)Fe2As2 (x=0 and 0.45) and SrFe2As2 single crystals
similarity 0.89M. S. Torikachvili et al.
Source status unknown — claims are unverified
Enhanced Superconductivity on the Tetragonal Lattice in FeSe under Hydrostatic Pressure
similarity 0.89Kiyotaka Miyoshi et al. · 2013 · arXiv:1310.7546
Source status unknown — claims are unverified
Pressure-induced antiferromagnetic transition and phase diagram in FeSe
similarity 0.89Taichi Terashima et al. · 2015 · arXiv:1502.03548
Source status unknown — claims are unverified
High-pressure polymorphism of BaFe2Se3
similarity 0.89V. Svitlyk et al. · 2018 · arXiv:1808.03952
Source status unknown — claims are unverified
Ab initio prediction of pressure-induced structural phase transition of superconducting FeSe
similarity 0.89Gul Rahman et al. · 2012 · arXiv:1201.5639
Source status unknown — claims are unverified