Enhanced Superconductivity on the Tetragonal Lattice in FeSe under Hydrostatic Pressure

Kiyotaka Miyoshi; Koh Morishita; Eriko Mutou; Masatoshi Kondo; Osamu Seida; Kenji Fujiwara; Jun Takeuchi; Shijo Nishigori

doi:10.7566/JPSJ.83.013702

Enhanced Superconductivity on the Tetragonal Lattice in FeSe under Hydrostatic Pressure

Kiyotaka Miyoshi, Koh Morishita, Eriko Mutou, Masatoshi Kondo, Osamu Seida, Kenji Fujiwara, Jun Takeuchi, Shijo Nishigori

arXiv:1310.7546 · DOI 10.7566/JPSJ.83.013702 · 2013-10-28 · Journal of the Physical Society of Japan

T1theoretical51 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Superconductivity under pressure in FeSe ($T_{\rm c}$$\sim$7.5 K) has been investigated using single-crystal specimens through the measurements of DC magnetization and electrical resistivity. A characteristic three-step increase in $T_{\rm c}$ has been found under hydrostatic pressure up to $\sim$34 K above 7 GPa. The structural transition from a tetragonal phase to an orthorhombic phase ($T_{\rm s}$$\sim$87 K) is found to disappear at $P$$\sim$2.3 GPa, above which $T_{\rm c}$ increases rapidly, suggesting that the superconductivity is enhanced by the tetragonal environment. Under non-hydrostatic pressure, the increase in $T_{\rm c}$ is suppressed and the superconductive volume fraction is considerably reduced above 2 GPa, probably owing to the breaking of the tetragonal lattice symmetry by the uniaxial stress. The intimate correlation between the enhanced (suppressed) superconductivity and the tetragonality (orthorhombicity) in the phase diagram is a common feature of FeSe and other iron-pnictide superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.5	Pressure unresolved	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	9.5	0.39 GPa	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	1.6 GPa	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	1.9 GPa	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	25	3 GPa	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	34	7.5 GPa	onset
LaFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	26	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	30	Pressure not reported	zero_resistance