Calculation of the transport critical current density of c-axis textured 122 iron-based superconductors

Lei Wang; Jinghui Xu; Duoduo Ba; Xianping Zhang; Zhaoshun Gao; Dongliang Wang; Yanwei Ma

doi:10.1016/j.physc.2012.12.003

← Back to search

Calculation of the transport critical current density of c-axis textured 122 iron-based superconductors

Lei Wang, Jinghui Xu, Duoduo Ba, Xianping Zhang, Zhaoshun Gao, Dongliang Wang, Yanwei Ma

arXiv:1211.1141 · DOI 10.1016/j.physc.2012.12.003 · 2012-11-06 · Physica C-superconductivity and Its Applications

T31 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The c-axis textured Sr1-xKxFe2As2 tapes produced by cold rolling and post-annealing, could carry a high super-current over 2*104 A/cm2. However, the magnitude is far from its maximum, because of the current obstacles associated with various defects in the material. To predict the maximal transport critical current density, we modeled the current paths in a c-axis textured polycrystal as a three-dimensional flow network, and calculated the maximum flow with the Ford-Fulkerson algorithm. It indicates that a much higher super-current of about 2*105 A/cm2 could be achieved in an ideal c-axis textured K-doped 122 polycrystal. The dependences of transport Jc on density, content of invalid boundary and grain size and shape were also studied. The results imply that, over 30% of the grain boundaries in the reported c-axis textured Sr1-xKxFe2As2 tapes may act as current obstacles, and the large ratio of width to thickness was expected to be the most favorable grain shape for high transport Jc in c-axis textured 122 superconducting tapes.