Large transport critical currents and magneto-optical imaging of textured Sr1-xKxFe2As2 superconducting tapes
Yanwei Ma, Chao Yao, Xianping Zhang, He Lin, Dongliang Wang, A. Matsumoto, H. Kumakura, Y. Tsuchiya, Y. Sun, T. Tamegai
arXiv:1302.4855 · DOI 10.1088/0953-2048/26/3/035011 · 2013-02-20 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report the temperature dependence of the transport critical current density (Jc) in textured Sr1-xKxFe2As2/Fe (Sr122) tapes fabricated by an ex situ powder-in-tube process. Critical currents were measured in magnetic fields up to 0-15 T and/or the temperature range 4.2-30 K by using a dc four-probe method. It was found that textured Sr122 tapes heat-treated at low temperatures showed higher transport Jc performance due to much improved intergrain connections. At temperatures of 20 K, easily obtained using a cryocooler, Jc reached ~ 10^4 A/cm^2 in self field, which is the highest transport value of ferropnictide wires and tapes reported so far. Magneto-optical imaging observations further revealed significant and well distributed global Jc at 20 K in our tapes. These results demonstrate that 122 type superconducting tapes are promising for high-field applications at around 20 K.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Sr1-xKxFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 20 | Pressure unresolved | unknown |
Similar papers
High transport critical current densities in textured Fe-sheathed Sr1-xKxFe2As2+Sn superconducting tapes
similarity 0.95Zhaoshun Gao et al. · 2011 · arXiv:1110.5784
Source status unknown — claims are unverified
High critical current density and low anisotropy in textured Sr1-xKxFe2As2 tapes for high field applications
similarity 0.94Zhaoshun Gao et al. · 2013 · arXiv:1302.4583
Source status unknown — claims are unverified
Hot pressing to enhance the transport Jc of Sr0.6K0.4Fe2As2 superconducting tapes
similarity 0.94He Lin et al. · 2014 · arXiv:1408.4516
Source status unknown — claims are unverified
Realization of practical level current densities in Sr0.6K0.4Fe2As2 tape conductors for high-field applications
similarity 0.93Xianping Zhang et al. · 2014 · arXiv:1403.6704
Source status unknown — claims are unverified
Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes
similarity 0.93Lei Wang et al. · 2009 · arXiv:0911.3701
Source status unknown — claims are unverified
Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes
similarity 0.91He Lin et al. · 2013 · arXiv:1309.7618
Source status unknown — claims are unverified