Effects of Annealing under Tellurium Vapor for Fe$_{1.03}$Te$_{0.8}$Se$_{0.2}$ Single Crystals

Yuta Koshika; Tomohiro Usui; Shintaro Adachi; Takao Watanabe; Kouhei Sakano; Shalamujiang Simayi; Masahito Yoshizawa

doi:10.7566/JPSJ.82.023703

← Back to search

Effects of Annealing under Tellurium Vapor for Fe$_{1.03}$Te$_{0.8}$Se$_{0.2}$ Single Crystals

Yuta Koshika, Tomohiro Usui, Shintaro Adachi, Takao Watanabe, Kouhei Sakano, Shalamujiang Simayi, Masahito Yoshizawa

arXiv:1212.6476 · DOI 10.7566/JPSJ.82.023703 · 2012-12-28 · Journal of the Physical Society of Japan

T1theoretical36 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In this study, the effects of annealing under tellurium vapor have been investigated for Fe$_{1.03}$Te$_{0.8}$Se$_{0.2}$ single crystals. The as-grown crystal is not superconducting. After annealing it at 400 $^\circ$C for 250 h in tellurium (Te) vapor, it shows metallic resistivity temperature dependence below 150 K and a sharp superconducting transition at 13 K. The sample also shows a full magnetic shielding effect at low temperatures. The improvement in superconductivity has been attributed to the removal of excess Fe, which is inevitably incorporated in the as-grown crystals, by the annealing.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Fe1+yTexSe1-x Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	14	Pressure not reported	unknown
Fe1.09Te0.83Se0.17 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	10	Pressure not reported	zero_resistance
Fe1.06Te0.83Se0.17 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	11	Pressure not reported	zero_resistance
Fe1.06Te0.83Se0.17 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	11	Pressure not reported	unknown
Fe1.00Te0.82Se0.18 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	Pressure not reported	zero_resistance
Fe1.00Te0.82Se0.18 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13	Pressure not reported	unknown