Effect of Vacuum Annealing on Superconductivity in Fe(Se,Te) Single Crystals
Seiki Komiya, Masafumi Hanawa, Ichiro Tsukada, Atsutaka Maeda
arXiv:1304.3590 · DOI 10.7566/JPSJ.82.064710 · 2013-04-12 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The effect of vacuum annealing on superconductivity is investigated in Fe(Se,Te) single crystals. It is found that superconductivity is not enhanced by annealing under high vacuum (~ 10^(-3) Pa) or by annealing in a sealed evacuated quartz tube. In a moderate vacuum atmosphere (~ 1 Pa), iron oxide layers are found to show up on sample surfaces, which would draw excess Fe out of the crystal. Thus, it is suggested that remanent oxygen effectively works to remove excess Fe from the matrix of Fe(Se,Te) crystals, resulting improvement of superconducting transition temperature. Our transport measurements suggest that the excess Fe scatters the carriers on electron- and hole-type channels in a different manner. We discuss how the mobility of two types of carriers correlate with superconductivity. Since both the electron and hole bands are important for the occurrence of superconductivity, excess Fe would suppress superconductivity mainly due to strong scattering of electrons.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Fe1.07Se0.29Te0.71 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
| Fe1.07Se0.29Te0.71 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
| Fe1.05Se0.3Te0.7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
| Fe1.05Se0.3Te0.7 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
Removal of excess iron by annealing processes and emergence of bulk superconductivity in sulfur-substituted FeTe
similarity 0.92Ryosuke Kurihara et al.
Source status unknown — claims are unverified
Bulk Superconductivity in FeTeSe Induced by Annealing in Se and S Vapor
similarity 0.91Yue Sun et al. · 2013 · arXiv:1310.1983
Source status unknown — claims are unverified
Thermal conductivity and annealing effects in the iron-based superconductor FeSeTe
similarity 0.91Masumi Ohno et al. · 2013 · arXiv:1306.2686
Source status unknown — claims are unverified
Incoherent-coherent crossover and the pseudogap in Te-annealed superconducting FeTeSe revealed by magnetotransport measurements
similarity 0.91Takumi Otsuka et al. · 2019 · arXiv:1904.13020
Source status unknown — claims are unverified
Revised Phase Diagram for FeTe1-xSex system with less excess Fe atoms
similarity 0.91Chihen Dong et al. · 2010 · arXiv:1012.5188
Source status unknown — claims are unverified
On the role of chalcogen vapor annealing in inducing bulk superconductivity in FeTeSe
similarity 0.91Wenzhi Lin et al. · 2015 · arXiv:1505.00271
Source status unknown — claims are unverified