Mechanochemical synthesis of pnictide compounds and superconducting Ba0.6K0.4Fe2As2 bulks with high critical current density
J. D. Weiss, J. Jiang, A. A. Polyanskii, E. E. Hellstrom
arXiv:1305.6820 · DOI 10.1088/0953-2048/26/7/074003 · 2013-05-29 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
BaFe2As2 (Ba-122) and (Ba0.6K0.4)Fe2As2 (K-doped Ba-122) powders were successfully synthesized from the elements using a reaction method, which incorporates a mechanochemical reaction using high-impact ball milling. Mechanically-activated, self-sustaining reactions (MSR) were observed while milling the elements together to form these compounds. After the MSR, the Ba-122 phase had formed, the powder had an average grain size < 1 μm, and the material was effectively mixed. X-ray diffraction confirmed Ba-122 was the primary phase present after milling. Heat treatment of the K-doped MSR powder at high temperature and pressure yielded dense samples with high phase purity but only granular current flow could be visualized by magneto optical imaging. In contrast, a short, low temperature, heat treatment at ambient pressure resulted in global current flow throughout the bulk sample even though the density was lower and impurity phases were more prevalent. An optimized heat treatment involving a two-step, low temperature, heat treatment of the MSR powder produced bulk material with very high critical current density above 0.1 MAcm-2 (4.2 K, 0 T).
Similar papers
Enhanced critical current properties in Ba0.6K0.4+xFe2As2 superconductor by over-doping of potassium
similarity 0.88Chunlei Wang et al. · 2011 · arXiv:1101.5427
Source status unknown — claims are unverified
Synthesis of Electron- and Hole-Doped Bulk BaFe2As2 Superconductors by Mechanical Alloying
similarity 0.87Kirill Pervakov & Vladimir Vlasenko · 2019 · arXiv:1912.07264
Source status unknown — claims are unverified
Utilization of mechanical alloying method for flux growth of single crystalline BaFe(AsP)
similarity 0.86Kosuke Z. Takahashi et al. · 2016 · arXiv:1604.08375
Source status unknown — claims are unverified
Fabrication and characterization of iron pnictide wires and bulk materials through the powder-in-tube method
similarity 0.86Yanwei Ma et al. · 2009 · arXiv:0906.3114
Source status unknown — claims are unverified
Superconductivity induced by Ni doping in BaFeAs
similarity 0.86L. J. Li et al. · 2008 · arXiv:0809.2009
Source status unknown — claims are unverified
Spatially - resolved study of the Meissner effect in superconductors using NV-centers-in-diamond optical magnetometry
similarity 0.85N. M. Nusran et al. · 2017 · arXiv:1709.02769
Source status unknown — claims are unverified