Utilization of mechanical alloying method for flux growth of single crystalline BaFe$_2$(As$_{1-x}$P$_x$)$_2$

Kosuke Z. Takahashi; Daisuke Okuyama; Taku J. Sato

doi:10.1016/j.jcrysgro.2016.04.047

← Back to search

Utilization of mechanical alloying method for flux growth of single crystalline BaFe$_2$(As$_{1-x}$P$_x$)$_2$

Kosuke Z. Takahashi, Daisuke Okuyama, Taku J. Sato

arXiv:1604.08375 · DOI 10.1016/j.jcrysgro.2016.04.047 · 2016-04-28 · Journal of Crystal Growth

T1theoretical1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Mechanical alloying method has been employed to prepare the Ba-Fe-As-P precursors, necessary for the Ba-(As,P) flux growth of the single crystalline BaFe$_2$(As$_{1-x}$P$_x$)$_2$. By alloying constituent elementals mechanically, the Ba-(As,P) precursors are successfully formed at the room temperature within one hour, significantly reducing preparation time. Using the mechanically alloyed precursors, we have grown single crystals of BaFe$_2$(As$_{1-x}$P$_x$)$_2$ with the sizes up to 5~mm $\times$ 5~mm $\times$ 0.1~mm.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
BaFe2(As1-xPx)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	31	Pressure not reported	onset
BaFe2(As0.669P0.331)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	27.6	Pressure not reported	midpoint
BaFe2(As0.687P0.313)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	27.3	Pressure not reported	midpoint
BaFe2(As0.47P0.53)2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	13.9	Pressure not reported	midpoint