Structural Analysis and Superconducting Properties of F-Substituted NdOBiS2 Single Crystals

Masanori Nagao; Satoshi Demura; Keita Deguchi; Akira Miura; Satoshi Watauchi; Takahiro Takei; Yoshihiko Takano; Nobuhiro Kumada; Isao Tanaka

doi:10.7566/JPSJ.82.113701

Structural Analysis and Superconducting Properties of F-Substituted NdOBiS2 Single Crystals

Masanori Nagao, Satoshi Demura, Keita Deguchi, Akira Miura, Satoshi Watauchi, Takahiro Takei, Yoshihiko Takano, Nobuhiro Kumada, Isao Tanaka

arXiv:1309.6400 · DOI 10.7566/JPSJ.82.113701 · 2013-09-25 · Journal of the Physical Society of Japan

T1experimental71 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of 1-2 mm and a well-developed ab-plane. The crystal structure of the grown crystals was determined by single-crystal X-ray diffraction analysis to be the tetragonal space group P4/nmm (#129) with a = 3.996(3) A and c = 13.464(6) A. The chemical formula of the grown crystals was approximately Nd0.98(0.06)O0.7(0.1)F0.3(0.1)Bi0.98(0.04)S2, and Cs, K, and Cl were not detected in the grown crystals by electron probe microanalysis. The grown crystals had a critical temperature of approximately 5 K. The superconducting anisotropy of the single crystals was estimated to be about 30 from the effective mass model and the upper critical field.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Nd0.98O0.7F0.3Bi0.98S2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5	Pressure not reported	unknown